Manganese dioxide for alkaline cells
View Patent ↗Particulate MnO 2 , having simultaneously a micropore surface area greater than 8.0 m 2 /g, desirably between about 8.0 and 13 m 2 /g and BET surface area of between about 20 and 31 m 2 /g within the context of an MnO 2 having a total intraparticle porosity of between about 0.035 cm 3 /g and 0.06 cm 3 /g produces enhanced performance when employed as cathode active material in an electrochemical cell, particularly an alkaline cell. The average pore radius of the meso and macro pores within the MnO 2 (meso-macro pore radius) is desirably greater than 32 Angstrom.
1. A particulate manganese dioxide having micropores and meso-macropores, said manganese dioxide having simultaneously a BET surface area between about 20 and 31 m 2 /g, a micropore area between about 8 and 13 m 2 /g and an average meso-macro pore radius greater than 32 Angstom, wherein said manganese dioxide is in particulate form and said micropores and meso-macro pores are intraparticle pores and the total porosity of said manganese dioxide, based on pores within the manganese dioxide, is between 0.035 cm 3 /g and 0.060 cm 3 /g, wherein the micropores are intraparticle pores having a diameter less than or equal to 20 Angstrom and the meso-macropores are pores having a diameter greater than 20 Angstrom.
2. The manganese dioxide of claim 1 wherein the manganese particles have an average diameter between about 1 and 100 micron.
3. The manganese dioxide of claim 1 wherein said manganese dioxide is an electrolytic manganese dioxide.
4. A particulate electrolytic manganese dioxide product having micropores and meso-macropores, said manganese dioxide having simultaneously a BET surface area between about 20 and 28 m 2 /g and a micropore area between 8 and 13 m 2 /g, and an average meso-macropore radius greater than about 32 Angstrom, wherein said manganese dioxide is in particulate form and said micropores and meso-macro pores are intraparticle pores and the total porosity, based on pores within the manganese dioxide, being between about 0.035 cm 3 /g and 0.040 cm 3 /g, wherein the micropores are intraparticle pores having a diameter less than or equal to 20 Angstrom and the meso-macropores are pores having a diameter greater than 20 Angstrom.
5. The electrolytic manganese dioxide of claim 4 wherein the manganese dioxide product is in particulate form having an average particle diameter between about 1 and 100 micron.
6. A particulate electrolytic manganese dioxide product having micropores and meso-macropores, said manganese dioxide having simultaneously a BET surface area between about 20 and 30 m 2 /g and a micropore area between 8 and 13 m 2 /g, and an average meso-macropore radius greater than about 32 Angstrom, wherein said manganese dioxide is in particulate form and said micropores and meso-macro pores are intraparticle pores and the total porosity, based on pores within the manganese dioxide, being between about 0.040 cm 3 /g and 0.045 cm 3 /g, wherein the micropores are intraparticle pores having a diameter less than or equal to 20 Angstrom and the meso-macropores are pores having a diameter greater than 20 Angstrom.
7. The electrolytic manganese dioxide of claim 6 wherein the manganese dioxide is in particulate form having an average particle diameter between about 1 and 100 micron.
8. A particulate electrolytic manganese dioxide product having micropores and meso-macropores, said manganese dioxide having simultaneously a BET surface area between about 20 and 31 m 2 /g and a micropore area between 8 and 13 m 2 /g, and an average meso-macropore radius greater than about 32 Angstrom, wherein said manganese dioxide is in particulate form and said micropores and meso-macro pores are intraparticle pores and the total porosity, based on pores within the manganese (dioxide, being between about 0.045 cm 3 /g and 0.050 cm 3 /g, wherein the micropores are intraparticle pores having a diameter less than or equal to 20 Angstrom and the meso-macropores are pores having a diameter greater than 20 Angstrom.
9. The electrolytic manganese dioxide of claim 8 wherein the manganese dioxide is in particulate form having an average particle diameter between about 1 and 100 micron.