Cationic or amphoteric copolymers prepared in an inverse emulsion matrix and their use in preparing cellulosic fiber compositions
View Patent ↗A papermaking method and a composition which utilize, as a drainage aid, a water-soluble cationic or amphoteric copolymer prepared via a water-in-oil polymerization technique that, absent a cross-linking agent, is characterized by a Huggins' constant (k′) determined in 0.01M NaCl greater than 0.3 and a storage modulus (G′) at 6.3 Hz greater than 50 Pa.
1. A copolymer composition comprising:
at least one associative inverse emulsion copolymer, wherein said at least one associative inverse emulsion copolymer has associative properties provided by at least one emulsification surfactant that is solely a triblock polymeric surfactant in which the surfactant to monomer ratio is at least 3:100 wherein said at least one associative inverse emulsion copolymer consists only of:
at least one nonionic polymer segment B consisting only of one or more ethylenically unsaturated nonionic monomers, and
at least one cationic polymer segment C consisting only of one or more ethylenically unsaturated cationic monomers;
the molar % ratio of B:C is from 99:1 to 1:99; and
wherein said at least one associative inverse emulsion copolymer has a Huggins' constant (k′) determined in 0.01 M NaCl greater than 0.5; and said at least one associative inverse emulsion copolymer has a storage modulus (G′) in a 3.0 wt % actives polymer solution at 6.3 Hz greater than 50 Pa.
2. The composition of claim 1 wherein B is selected from the group consisting of acrylamide, methacrylamide; N-alkylacrylamides, N,N-dialkyl-acrylamide; methyl methacrylate, methyl acrylate; acrylonitrile; N-vinyl methylacetamide; N-vinylformamide; N-vinylmethyl formamide; vinyl acetate; N-vinyl pyrrolidone; and mixtures of any of the foregoing.
3. The composition of claim 1 wherein C is selected from the group consisting of diallyldialkylammonium halides, (meth)acrylates of dialkylaminoalkyl compounds, such as dimethylaminoethyl (meth)acrylate, diethylaminoethyl (meth)acrylate, dimethyl aminopropyl (meth)acrylate, 2-hydroxydimethyl aminopropyl (meth)acrylate, aminoethyl (meth)acrylate, and the salts and quaternaries thereof; the N,N-dialkylaminoalkyl(meth)acrylamides, such as N,N-dimethylaminoethylacrylamide, and the salt and quaternaries thereof and mixtures of any of the foregoing.
4. The composition of claim 1 wherein the triblock surfactant is a copolymer based on polyester derivatives of fatty acids and poly(ethyleneoxide).
5. The composition of claim 1 further comprising cellulose fiber.
6. A method of making a cellulose fiber composition which comprises adding to a cellulose pulp slurry the water-soluble cationic copolymer of claim 1 .
7. The composition of claim 1 wherein the emulsification surfactant consists of a blend of a polymeric surfactant comprising one or two polymeric components derived from oil-soluble complex monocarboxylic acid and a water-soluble component derived from polyalkylene glycol, and sorbitan monooleate; and 2,2′-azobisisobutyronitrile is employed as the free radical initiator.
8. The composition of claim 7 wherein the surfactant system has a combined Hydrophilic-Lipophilic Balance of less than 8.
9. The composition of claim 8 wherein the triblock surfactant is a copolymer based on polyester derivatives of fatty acids and poly(ethyleneoxide).
10. The composition of claim 1 wherein the ratio of B:C is about 99:1 to about 50:50.
11. The composition of claim 10 wherein the ratio of B:C is about 95:5 to about 50:50.
12. The composition of claim 1 wherein k′ is greater than 0.6.
13. The composition of claim 1 wherein G′ is greater than 75.
14. A copolymer composition comprising:
at least one structured inverse emulsion copolymer, wherein said at least one structured inverse emulsion copolymer has associative properties provided by at least one emulsification surfactant that is a triblock polymeric surfactant in which the surfactant to monomer ratio is at least 3:100 wherein said at least one structured inverse emulsion copolymer consists only of:
at least one nonionic polymer segment B consisting only of one or more ethylenically unsaturated nonionic monomers, and
at least one cationic polymer segment C consisting only of one or more ethylenically unsaturated cationic monomers;
the molar % ratio of B:C is from 99:1 to 1:99; and
wherein said at least one structured inverse emulsion copolymer has a Huggins' constant (k′) determined in 0.01 M NaCl greater than 0.5; and said at least one structured inverse emulsion copolymer has a storage modulus (G′) in a 3.0 wt % actives polymer solution at 6.3 Hz greater than 50 Pa.