Photoluminescent phosphor powders, methods for making phosphor powders and devices incorporating same
View Patent ↗Photoluminescent phosphor powders and a method for making phosphor powders. The phosphor powders have a small particle size, narrow particle size distribution and are substantially spherical. The method of the invention advantageously permits the economic production of such powders. The invention also relates to improved devices, such as display devices and lighting elements, incorporating the phosphor powders.
1. A photoluminescent device comprising:
a) an excitation source; and
b) at least a first layer of photoluminescent phosphor particles adapted to be stimulated by said excitation source and which are selected from the group consisting of Y 2 O 3 :Eu, (Y,Gd)BO 3 :Eu, Zn 2 SiO 4 :Mn, barium aluminate and doped barium magnesium aluminate, wherein said phosphor particles have a weight average particle size of from about 0.1 μm to about 10 μm, a substantially spherical morphology and wherein at least about 80 weight percent of said particles are not larger than two times said average particle size.
2. A photoluminescent device as recited in claim 1 , wherein said phosphor particles have an average size of from about 0.3 μm to about 5 μm.
3. A photoluminescent device as recited in claim 1 , wherein said excitation source comprises a gas and wherein said gas comprises xenon.
4. A photoluminescent device as recited in claim 1 , wherein said excitation source comprises a gas and wherein said gas comprises mercury.
5. A photoluminescent device as recited in claim 1 , wherein said particles comprise Y 2 O 3 :Eu.
6. A photoluminescent device as recited in claim 1 , wherein said particles comprise (Y,Gd)BO 3 :Eu.
7. A photoluminescent device as recited in claim 1 , wherein said particles comprise Zn 2 SiO 4 :Mn.
8. A photoluminescent device as recited in claim 1 , wherein said particles comprise barium magnesium aluminate doped with Eu.
9. A photoluminescent device as recited in claim 1 , wherein said particles comprise barium aluminate.
10. A photoluminescent device as recited in claim 1 , wherein said particles comprise barium magnesium aluminate doped with Mn.
11. A photoluminescent device as recited in claim 1 , wherein said layer is a substantially uniform layer of photoluminescent phosphor particles, said layer having an average thickness of not greater than about three times said average particle size.
12. A photoluminescent device as recited in claim 1 , wherein said device is a plasma display panel.
13. A photoluminescent device as recited in claim 1 , wherein said device is a fluorescent lamp.
14. A photoluminescent device as recited in claim 1 , wherein said device is an LCD backlight.
15. A plasma display panel, comprising:
a) a rear panel comprising a plurality of row electrodes;
b) a front panel comprising a plurality of column electrodes, wherein said row electrodes and said column electrodes are in perpendicular relation to form a plurality of addressable x-y coordinates;
c) a photoluminescent phosphor powder dispersed on a substrate disposed between said electrodes, wherein said phosphor powder comprises particles having a host material selected from the group consisting of oxides, silicates, aluminates and borates, and having a substantially spherical morphology, a weight average particle size of not greater than about 5 μm and a particle size distribution wherein at least about 80 weight percent of said particles are not larger than two times said average particle size.
16. A plasma display panel as recited in claim 15 , wherein said average particle size is from about 0.3 μm to about 5 μm.
17. A plasma display panel as recited in claim 15 , wherein said particles have a particle size distribution wherein at least about 90 weight percent of said particles are not larger than about two times said weight average particle size.
18. A plasma display panel as recited in claim 15 , wherein said phosphor particles comprise crystallites having an average crystallite size of at least about 25 nanometers.
19. A plasma display panel as recited in claim 15 , wherein said phosphor powder is dispersed in a substantially uniform layer having an average thickness of not greater than about three times said average particle size.
20. A plasma display panel as recited in claim 15 , wherein said phosphor powder comprises barium magnesium aluminate doped with Eu.
21. A plasma display panel as recited in claim 15 , wherein said phosphor powder comprises barium magnesium aluminate and from about 8 to about 12 atomic percent Eu and wherein said plasma display panel comprises xenon gas as an excitation source.
22. A plasma display panel as recited in claim 15 , wherein said phosphor powder comprises barium aluminate doped with Mn.
23. A plasma display panel as recited in claim 15 , wherein said phosphor powder comprises barium aluminate and from about 8 to about 12 atomic percent Mn and wherein said plasma display panel comprises xenon gas as an excitation source.
24. A plasma display panel as recited in claim 15 , wherein said phosphor powder comprises Zn 2 SiO 4 :Mn.
25. A plasma display panel as recited in claim 15 , wherein said phosphor powder comprises Zn 2 SiO 4 and from about 0.05 to about 2 atomic percent Mn and wherein said plasma display panel comprises xenon gas as an excitation source.
26. A plasma display panel as recited in claim 15 , wherein said phosphor powder comprises Y 2 O 3 :Eu.
27. A plasma display panel as recited in claim 15 , wherein said phosphor powder comprises Y 2 O 3 and from about 4 to about 6 atomic percent Eu and wherein said plasma display panel comprises xenon gas as an excitation source.
28. A plasma display panel as recited in claim 15 , wherein said phosphor powder comprises (Y,Gd)BO 3 :Eu.
29. A plasma display panel as recited in claim 15 , wherein said phosphor powder comprises (Y,Gd)BO 3 and from about 14 to about 20 atomic percent Eu and wherein said plasma display panel comprises xenon gas as an excitation source.
30. A plasma display panel as recited in claim 15 , wherein said phosphor powder comprises:
a) first phosphor particles of barium magnesium aluminate doped with Eu;
b) second phosphor particles selected from the group consisting of Zn 2 SiO 4 :Mn, barium aluminate doped with Mn and mixtures thereof; and
c) third phosphor particles selected from the group consisting of Y 2 O 3 :Eu, (Y,Gd)BO 3 :Eu and mixtures thereof.