Hydrothermally stable metal promoted zeolite beta for NO
A stabilized metal promoted aluminosilicate zeolite, useful in the selective catalytic reduction of nitrogen oxides with ammonia, having a silica to alumina mole ratio of at least 8 and less than 30 and an FT-IR absorption peak at 3781 plus or minus 2 cm −1 which stabilizes the zeolite against further dealumination such as under oxidizing and harsh hydrothermal conditions.
1. A stabilized metal-promoted aluminosilicate zeolite having a silica to alumina mol ratio of at least 8 and less than 30 and an FT-IR absorption peak at 3781±2 cm −1 , and wherein said metal is copper or iron.
2. The stabilized aluminosilicate zeolite of claim 1 , wherein said zeolite has a pore structure which is interconnected in all three crystallographic dimensions by pores having an average kinetic pore diameter of at least about 7 Å.
3. The stabilized aluminosilicate zeolite of claim 2 , wherein said zeolite is selected from the group consisting of ultrastable Y, beta and ZSM-20.
4. The stabilized aluminosilicate zeolite of claim 1 selected from the group consisting of ZSM-5, ZSM-8, ZSM-11, ZSM-12, zeolite X, zeolite Y, beta, mordenite and erionite.
5. The stabilized aluminosilicate zeolite of claim 1 , wherein said zeolite is zeolite beta.
6. The stabilized aluminosilicate zeolite of claim 1 , wherein said metal promoter is present in amounts of 0.1 to 30 percent by weight calculated as metal and based on the total weight of the metal and the zeolite.
7. The stabilized aluminosilicate zeolite of claim 1 , wherein said zeolite is zeolite beta and said metal promoter is iron.
8. The stabilized aluminosilicate zeolite of claim 1 , wherein said iron is present in amounts of from 0.5 to 2.5 weight percent.
9. The stabilized aluminosilicate zeolite of claim 1 , wherein said iron is present in amounts of from 0.7 to 1.5 weight percent.
10. The stabilized metal-promoted aluminosilicate zeolite of claim 1 , wherein said silica to alumina mol ratio is from at least 8 to 28.
11. A stabilized aluminosilicate zeolite catalyst characterized by a silica to alumina mol ratio of at least 8 and less than 30 and by FT-IR absorption peak at 3781±2 cm −1 and wherein said peak has an area of at least 0.05 absorbance unit x cm −1 , and wherein said zeolite is promoted with a metal and said metal is copper or iron.
12. The stabilized aluminosilicate zeolite of claim 11 , wherein said zeolite has a pore structure which is interconnected in all three crystallographic dimensions by pores having an average kinetic pore diameter of at least about 7 Å.
13. The stabilized aluminosilicate zeolite of claim 12 , wherein said zeolite is selected from the group consisting of ultrastable Y, beta and ZSM-20.
14. The stabilized aluminosilicate zeolite of claim 12 , wherein said zeolite is zeolite beta.
15. The stabilized aluminosilicate zeolite of claim 11 , wherein said zeolite is ion-exchanged with said copper or iron.
16. The stabilized aluminosilicate zeolite of claim 15 , wherein said copper or iron comprises 0.1 to 30 weight percent by weight calculated as the metal and based on the total weight of the metal and the zeolite.
17. The stabilized aluminosilicate zeolite of claim 16 , wherein said zeolite is beta and said metal is iron.
18. The stabilized aluminosilicate zeolite catalyst of claim 11 , wherein said silica to alumina mol ratio is from at least 8 to 28.