Barrier coating of a non-elastomeric polymer and a dispersed layered filler in a liquid carrier and coated articles
View Patent ↗Barrier coating mixtures contain in a carrier liquid, (a) a non-elastomeric polymer; (b) an exfoliated layered platelet-like silicate filler which may or may not have been acid or base treated that has not been functionalized with organic cations having an aspect ratio greater than 25; and (c) at least one additive, wherein the total solids content is less than 30% and the amount of filler is between 5% to about 60% of the total solids content. Coated articles and containers, freestanding films and packaging films are produced using the barrier coating mixtures. Methods of manufacturing such coated products are also encompassed.
1. A barrier coating derived from a stable aqueous dispersion where said dispersion is in the form of an emulsion, suspension, colloidal dispersion and/or latex, said dispersion including (i) a dispersed non-elastomeric polymer selected from the group consisting of polyvinylidene chlorides, polyesters, polyacrylics and polyurethanes, (ii) a dispersed substantially exfoliated silicate filler material not functionalized with organic cations, the silicate filler having an aspect ratio greater than 25 wherein said substantially exfoliated silicate filler is treated with acid or base prior to being combined with the non-elastomeric polymer, and wherein % of the silicate filler is less than 60% of the solid content based on weight, and (iii) at least one additive, selected from the group consisting of surfactants, emulsifiers, anti-foaming agents, dispersing agents, wetting agents, leveling agents and thickeners wherein the coating exhibits an at least 5-fold reduction in gas permeability than a coating formed of said non-elastomeric polymer alone.
2. The barrier coating according to claim 1 wherein said coating exhibits an at least 25-fold reduction in gas permeability as compared with a coating formed of said non-elastomeric polymer alone.
3. The barrier coating according to claim 2 wherein said coating exhibits an at least 50-fold reduction in gas permeability as compared with a coating formed of said non-elastomeric polymer alone.
4. The barrier coating according to claim 3 wherein said coating exhibits an at least 100-fold reduction in gas permeability as compared with a coating formed of said non-elastomeric polymer alone.
5. The barrier coating according to claim 4 wherein said coating exhibits an at least 500-fold reduction in gas permeability as compared with a coating formed of said non-elastomeric polymer alone.
6. The barrier coating according to claim 5 wherein said coating exhibits an at least 1000-fold reduction in gas permeability as compared with a coating formed of said non-elastomeric polymer alone.
7. The barrier coating according to claim 1 wherein said non-elastomeric polymer is a polyvinylidene chloride containing polymer.
8. The barrier coating according to claim 7 wherein said non-elastomeric polymer is a polyvinylidene chloride/polyvinyl chloride copolymer.
9. The barrier coating according to claim 1 wherein said non-elastomeric polymer is a polyester with a T g lower than 70° C.
10. The barrier coating according to claim 9 wherein said non-elastomeric polymer is a polyester with a T g lower than 35° C.
11. The barrier coating according to claim 1 wherein said silicate filler is selected from the group consisting of bentonite, vermiculite, montmorillonite, nontronite, beidellite, volkonskoite, hectorite, saponite, laponite, sauconite, magadiite, kenyaite, ledikite and mixtures or solutions of the above silicates.
12. The barrier coating of claim 11 wherein said silicate filler is vermiculite.
13. The barrier coating of claim 1 wherein said acid is selected from the group consisting of acetic acid, glycine and citric acid.
14. The barrier coating of claim 1 wherein said base is selected from the group consisting of ammonium hydroxide, sodium hydroxide and potassium hydroxide.
15. The barrier coating according to claim 1 wherein said silicate filler is present in said dispersion at between 10 to about 50% of the total solids content of the dispersion, based on weight.
16. The barrier coating according to claim 1 wherein said dispersion has a total solids content of from about 5 to about 25%, based on weight.
17. A method to produce a barrier coating film comprising:
a) applying to a substrate an aqueous dispersion containing a dispersed non-elastomeric polymer selected from the group consisting of polyvinylidene chlorides, polyesters, polyacrylics and polyurethanes, a dispersed substantially exfoliated silicate filler material not functionalized with organic cations, the silicate filler having an aspect ratio greater than 25, wherein said substantially exfoliated silicate filler is treated with acid or base prior to being combined with the non-elastomeric polymer, wherein % of the silicate is less than 60% of the solid content based on weight, and at least one additive, selected from the group consisting of surfactants, emulsifiers, anti-foaming agents, dispersing agents, wetting agents, leveling agents and thickeners;
b) drying the dispersion to a barrier coating having the same polymer to filler ratio as in said dispersion wherein the coating exhibits an at least 5-fold reduction in gas permeability than a coating formed of said non-elastomeric polymer alone.
18. The method according to claim 17 wherein said dispersion is in a form selected from the group consisting of a dispersion, an emulsion, a suspension and a latex.
19. The method according to claim 17 wherein said non-elastomeric polymer is a polyvinylidene chloride containing polymer.
20. The barrier coating according to claim 19 wherein said non-elastomeric polymer is a polyvinylidene chloride/polyvinyl chloride copolymer.
21. The method according to claim 17 wherein said non-elastomeric polymer is a polyester with a T g lower than 70° C.
22. The method according to claim 21 wherein said non-elastomeric polymer is a polyester with a T g lower than 35° C.
23. The method according to claim 17 wherein said silicate filler is selected from the group consisting of bentonite, vermiculite, montmorillonite, nontronite, beidellite, volkonskoite, hectorite, saponite, laponite, sauconite, magadiite, kenyaite, ledikite and mixtures of the above silicates.
24. The method of claim 23 wherein said silicate filler is vermiculite.
25. The method of claim 17 wherein said acid is selected from the group consisting of acetic acid, glycine and citric acid.
26. The method of claim 17 wherein said base is selected from the group consisting of ammonium hydroxide, sodium hydroxide and potassium hydroxide.
27. The method according to claim 17 wherein said dispersed silicate is present in said dispersion at between 10 to about 50% of the total solids content, based on weight.
28. The method according to claim 17 wherein said dispersion has a total solids content of from about 5 to about 25%, based on weight.
29. The method according to claim 17 wherein said substrate is selected from the group consisting of antiseptic packaging films, corrosion protective films, vacuum and controlled atmosphere packages, blow molded containers, thermoformed containers and electronic display films.
30. A barrier coating derived from a mixture of:
a) an aqueous dispersed non-elastomeric polymer selected from the group consisting of polyvinylidene chlorides, polyesters, polyacrylics and polyurethanes; and
b) an aqueous dispersed, exfoliated silicate filler having an aspect ratio greater than 25, wherein the aqueous dispersed, exfoliated silicate filler is treated with acid or base prior to being mixed with the dispersed, non-elastomeric polymer;
wherein the mixture further includes at least one additive, selected from the group consisting of surfactants, emulsifiers, anti-foaming agents, dispersing agents, leveling agents and thickeners,
and wherein the coating exhibits an at least 100-fold reduction in gas permeability than a coating formed of said non-elastomeric polymer alone.
31. A barrier coating derived from a stable aqueous coating formulation which is in the form of an emulsion, a suspension, a latex, a colloidal dispersion, or combinations thereof, and wherein the formulation includes:
a) a dispersed non-elastomeric polymer selected from the group consisting of polyvinylidene chlorides, polyesters, polyacrylics and polyurethanes;
b) a dispersed exfoliated silicate filler having an aspect ratio greater than 25, wherein the aqueous dispersed, exfoliated silicate filler, is treated with acid or base prior to being mixed with the dispersed, non-elastomeric polymer; and
c) at least one additive selected from the group consisting of surfactants, emulsifiers, anti-foaming agents, dispersing agents, leveling agents, and thickeners,
wherein further the coating exhibits an at least 500-fold reduction in gas permeability than a coating formed of said non-elastomeric polymer alone.
32. A barrier coating derived from a stable aqueous dispersion where said dispersion is in the form of an emulsion, suspension, colloidal dispersion and/or latex, said dispersion including (i) a dispersed non-elastomeric polymer selected from the group consisting of polyvinylidene chlorides, polyesters, polyacrylics and polyurethanes, (ii) a dispersed substantially exfoliated silicate filler material not functionalized with organic cations, the silicate filler having an aspect ratio greater than 25 wherein said substantially exfoliated silicate filler is treated with acid or base prior to being combined with the non-elastomeric polymer, and wherein % of the silicate filler is less than 60% of the solid content based on weight, and (iii) at least one additive, selected from the group consisting of surfactants, emulsifiers, anti-foaming agents, dispersing agents, wetting agents, leveling agents and thickeners wherein the coating exhibits an at least 2-fold reduction in gas permeability as compared with a like coating formed with untreated filler.
33. The barrier coating according to claim 32 wherein said coating exhibits an at least 5-fold reduction in permeability as compared with a like coating formed with untreated filler.
34. The barrier coating according to claim 32 wherein said coating exhibits an at least 10-fold reduction in permeability as compared with a like coating formed with untreated filler.
35. A method to produce a barrier coating film comprising:
a) applying to a substrate an aqueous dispersion containing a dispersed non-elastomeric polymer selected from the group consisting of polyvinylidene chlorides, polyesters, polyacrylics and polyurethanes, a dispersed substantially exfoliated silicate filler material not functionalized with organic cations, the silicate filler having an aspect ratio greater than 25, wherein said substantially exfoliated silicate filler is treated with acid or base prior to being combined with the non-elastomeric polymer, wherein % of the silicate is less than 60% of the solid content based on weight, and at least one additive, selected from the group consisting of surfactants, emulsifiers, anti-foaming agents, dispersing agents, wetting agents, leveling agents and thickeners;
b) drying the dispersion to a barrier coating having the same polymer to filler ratio as in said dispersion wherein the coating exhibits an at least 2-fold reduction in gas permeability as compared with a like coating formed with untreated filler.
36. The method according to claim 35 wherein the barrier coating exhibits an at least 5-fold reduction in gas permeability as compared with a like coating formed with untreated filler.
37. The method according to claim 35 wherein the barrier coating exhibits an at least 10-fold reduction in gas permeability as compared with a like coating formed with untreated filler.
38. A barrier coating derived from a stable aqueous coating formulation which is in the form of an emulsion, a suspension, a latex, a colloidal dispersion, or combinations thereof, and wherein the formulation includes:
a) a dispersed non-elastomeric polymer selected from the group consisting of polyvinylidene chlorides, polyesters, polyacrylics and polyurethanes;
b) a dispersed exfoliated silicate filler having an aspect ratio greater than 25, wherein the aqueous dispersed, exfoliated silicate filler, is treated with acid or base prior to being mixed with the dispersed, non-elastomeric polymer; and
c) at least one additive selected from the group consisting of surfactants, emulsifiers, anti-foaming agents, dispersing agents, leveling agents, and thickeners,
wherein further the coating exhibits an at least 2-fold reduction in gas permeability as compared with a like coating formed with untreated filler.
39. The barrier coating according to claim 38 wherein said coating exhibits an at least 5-fold reduction in permeability as compared with a like coating formed with untreated filler.
40. The barrier coating according to claim 38 wherein said coating exhibits an at least 10-fold reduction in permeability as compared with a like coating formed with untreated filler.