Aqueous superabsorbent polymer and methods of use
View Patent ↗The present invention relates to a crosslinked aqueous solution polymer composition consisting of about 15 wt-% to about 50 wt-% of at least one water soluble monomer, preferably an alpha, beta-ethylenically unsaturated carboxylic acid monomer and a crosslinking agent. The polymer solution is sufficiently low enough in viscosity such that it can be applied in aqueous form, yet after crosslinking possesses a fast rate of acquisition and is high absorption capacity. The invention also relates to new methods of enhancing the absorbency of various articles, increasing the humectancy and/or absorbency of a fiber or fibrous matrix, improving the water retention of soil and other agricultural methods, and increasing the open time of cement by incorporating or applying an aqueous superabsorbent polymer composition.
1. A method of increasing the absorbency of an article, said method comprising:
a) applying an aqueous polymer composition on an absorbent article, said aqueous polymer composition comprising
i) a polymer derived from monomers consisting of water soluble α-β-ethylenically unsaturated carboxylic acid monomers, said polymer having been from about 75% to 95% neutralized with a base selected from the group consisting of alkali metal hydroxide, alkaline earth metal hydroxide and combinations thereof, said polymer having been further neutralized with a volatile base to a pH of at least 7; and
ii) a crosslinking agent,
said composition having a viscosity of from about 50 cPs to about 20,000 cPs at 25° C.; and
b) drying said composition.
2. The method of claim 1 , wherein said α-β-ethylenically unsaturated carboxylic acid is selected from the group consisting of methacrylic acid, crotonic acid, maleic acid, maleic acid anhydride, itaconic acid, and fumaric acid.
3. The method of claim 1 , wherein said polymer comprises polyacrylic acid.
4. The method of claim 1 , wherein said alkali metal hydroxide is selected from the group consisting of sodium hydroxide, potassium hydroxide and mixtures thereof.
5. The method of claim 1 , wherein said alkaline earth metal hydroxide comprises calcium hydroxide.
6. The method of claim 1 , wherein said volatile base comprises ammonium hydroxide.
7. The method of claim 1 , having a viscosity of from about 100 cPs to about 5,000 cPs at 25° C.
8. The method of claim 1 , wherein the ratio of the weight of said polymer to the weight of said crosslinking agent is about 10 to 1.
9. The method of claim 1 , wherein said crosslinking agent is ammonium zirconyl carbonate.
10. The method of claim 1 , wherein said crosslinking agent is selected from the group consisting of zirconium ions and aziridine.
11. The method of claim 1 , wherein said composition, when dry, absorbs at least 50 times its polymer weight in water.
12. The method of claim 1 , wherein said composition, when dry, absorbs from 50 times to 150 times its polymer weight in water.
13. The method of claim 1 , wherein said substrate is selected from the group consisting of diapers, sanitary napkins, paper towels and facial tissue.
14. A method of making a superabsorbent article comprising:
a) contacting a substrate with an aqueous polymer composition comprising
i) a polymer derived from monomers consisting of water soluble α-β-ethylenically unsaturated carboxylic acid monomers, said polymer having been from about 75% to 95% neutralized with a base selected from the group consisting of alkali metal hydroxide, alkaline earth metal hydroxide and combinations thereof, said polymer having been further neutralized with a volatile base to a pH of at least 7; and
ii) a crosslinking agent,
said composition having a viscosity of from about 50 cPs to about 20,000 cPs at 25° C.; and
b) drying said composition.
15. A method of making a superabsorbent article comprising:
a) contacting a substrate with an aqueous polymer composition comprising
i) a homopolymer of an α-β-ethylenically unsaturated carboxylic acid monomer, said homopolymer having been from about 75% to 95% neutralized with a base selected from the group consisting of alkali metal hydroxide, alkaline earth metal hydroxide and combinations thereof, said homopolymer having been further neutralized with a volatile base to a PH of at least 7; and
ii) a crosslinking agent,
said composition having a viscosity of from about 50 cPs to about 20,000 cPs at 25° C.; and
b) drying said composition.