View Patent ↗A fluorocopolymer which comprises (A) polymerized units based on tetrafluoroethylene, (B) polymerized units based on ethylene and (C) polymerized units based on itaconic anhydride or citraconic anhydride, wherein the molar ratio of (A)/(B) is from 20/80 to 80/20, and the molar ratio of (C)/((A)+(B)) is from 1/10000 to 5/100, and which has a volume flow rate of from 1 to 1000 mm 3 /sec. The fluorocopolymer is excellent in the fuel barrier properties and in the adhesive properties to a non-fluorinated polymer.
1. A multi-layer laminate hose having a fluorocopolymer layer and a polyamide resin layer directly laminated thereto, wherein the fluorocopolymer comprises (A) polymerized units of tetrafluoroethylene, (B) polymerized units of ethylene and (C) polymerized units of itaconic anhydride or citraconic anhydride, in which the molar ratio of (A)/(B) is from 20/80 to 80/20, and the molar ratio of (C)/((A)+(B)) is from 1/10000 to 5/100, and which has a volume flow rate of from 1 to 1000 mm 3 /sec.
2. The multi-layer laminate hose according to claim 1 , wherein the molar ratio of(C)/((A)+(B)) is from 1/1000 to 5/100.
3. The multi-layer laminate hose according to claim 1 , wherein the laminate is obtained by co-extrusion molding.
4. The multi-layer laminate hose according to claim 1 , wherein the laminate is obtained by co-extrusion molding.
5. The multilayer laminate of claim 1 , wherein the fluorocopolymer further comprises (D) polymerized units of another monomer, in an amount of from 0.01 to 20 mol %, based on the total polymerized units in the fluorocopolymer.
6. The multilayer laminate according to claim 5 , wherein said another monomer is a compound represented by CH 2 -(CX(CF 2 ) n Y wherein each of X and Y which are independent of each other, is a hydrogen atom or a fluorine atom, and n is an integer of from 2 to 8.
7. The multilayer laminate according to claim 6 , wherein n is from 2 to 4.
8. The multilayer laminate according to claim 1 , wherein the molar ratio of (A)/(B) is from 50/50 to 60/40.
9. The multilayer laminate according to claim 1 , wherein the molar ratio of(C)/((A)+(B)) is from 3/2000 to 3/100.
10. The multilayer laminate according to claim 1 , wherein said another monomer is CH 2 ═CH(CF 2 ) n F, wherein n is from 2 to 4.
11. The multilayer laminate according to claim 1 , wherein the molar ratio of(C)/((A)+(B)) is from 3/1000 to 3/100.
12. The multilayer laminate according to claim 1 , wherein the volume flow rate is from 5 to 500 mm 3 /sec.
13. The multilayer laminate according to claim 1 , wherein the volume flow rate is from 10 to 200 mm 3 /sec.
14. The multilayer laminate according to claim 1 , wherein the fluorocopolymer has a functional group reactive with a non-fluorinated polymer, wherein the functional group is selected from the group consisting of an ester group, a carbonate group, a hydroxyl group, a carboxyl group, a carbonyl fluoride group or a combination thereof.
15. The multilayer laminate according to claim 1 , wherein the polymerized units (C) are present in an amount of from 0.01 to 5% based on the total molar ratio of tetrafluoro ethylene and ethylene.
16. The multilayer laminate according to claim 1 , wherein the polymerized units (C) are present in an amount of from 0.1 to 1% based on the total molar ratio of tetrafluoroethylene and ethylene.
17. The multilayer laminate according to claim 1 , further comprising polymerized units of a vinyl ester (E).
18. The multilayer laminate according to claim 17 , wherein the vinyl ester is selected from the group consisting of vinyl acetate, vinyl chloroacetate, vinyl butanoate and vinyl pivalate.
19. The multilayer laminate according to claim 1 , wherein the fluorocopolymer further comprises polymerized units of vinyl acetate.
20. The multilayer laminate according to claim 6 , further comprising polymerized units of vinyl acetate.
21. The multilayer laminate according to claim 1 , wherein the multilayer laminate is in the shape of a tube.