Lithium metal dispersion in secondary battery anodes
View Patent ↗The present invention is a secondary battery having a high specific capacity and good cycleability, and that can be used safely. The secondary battery is manufactured to include an anode formed from a host material capable of absorbing and desorbing lithium in an electrochemical system such as a carbonaceous material, and lithium metal dispersed in the host material. The freshly prepared anodes of the invention are combined with a positive electrode including an active material, a separator that a separates the positive electrode and the negative electrode, and an electrolyte in communication with the positive electrode and the negative electrode. The present invention also includes a method of preparing a freshly prepared anode and a method of operating a secondary battery including the anode of the invention.
1. A method of preparing an anode for a secondary battery comprising:
providing a host material that is capable of absorbing and desorbing lithium in an electrochemical system;
dispersing an amount of lithium metal in the host material wherein the amount is no more than the maximum amount sufficient to intercalate in, alloy with, or be absorbed by the host material in the anode; and
forming the host material and the lithium metal dispersed therein into the anode.
2. The method according to claim 1 , wherein said dispersing step comprises mixing the lithium metal, the host material and a non-aqueous liquid together to form a slurry.
3. The method according to claim 2 , wherein said forming step comprising applying the slurry to a current collector and drying the slurry.
4. The method according to claim 1 , wherein said dispersing step comprises immersing the host material in a suspension containing lithium metal and a non-aqueous liquid.
5. The method according to claim 4 , wherein said dispersing step comprises immersing the host material in a suspension of lithium metal in a hydrocarbon.
6. The method according to claim 1 , wherein said dispersing step comprises dispersing lithium metal having a mean particle size of less than about 20 microns in the host material.
7. The method according to claim 1 , wherein said providing step includes providing a host material comprising one or more materials capable of reversibly lithiating and delithiating at an electrochemical potential versus lithium of from greater than 0.0 V to less than or equal to 1.5 V.
8. The method according to claim 1 , wherein said providing step comprises providing a host material comprising one or more materials selected from the group consisting of carbonaceous materials, Si, Sn, tin oxides, composite tin alloys, transition metal oxides, lithium metal nitrides, and lithium metal oxides.
9. The method according to claim 1 , wherein said providing step comprises providing a host material comprising a carbonaceous material.
10. The method according to claim 9 , wherein said providing step comprises providing a host material wherein the carbonaceous material is graphite.
11. The method according to claim 10 , wherein said providing step comprises providing a host material wherein the host material further comprises carbon black.