Steel for use in high strength pinion shaft and manufacturing method thereof
A steel for use in high strength pinion shaft which is not refined and used by applying high frequency hardening, with less occurrence of peeling during hobbing, having high surface hardness, impact value and torsional strength after high frequency hardening, and with less heat treatment strains during high frequency hardening, containing, on the mass % basis; C: 0.45-0.55%, Si: 0.10-0.50%, Mn: 0.50-1.20%, P: 0.025% or less, S: 0.025% or less, Mo: 0.15-0.25%, B: 0.0005-0.005%, Ti: 0.005-0.10%, and N: 0.015% or less, satisfying: 0.80≦Ceq 0.95 and f value≦1.0, and the balance of Fe and inevitable impurities, as well as a manufacturing method thereof.
1. A method of manufacturing a steel for use in a high strength pinion shaft comprising:
providing a steel;
hot rolling the steel at a temperature of 700° C. to 850° C. under a draft ratio at an area reduction of 10%; and
high frequency hardening the steel,
wherein a hardness of said steel before the high frequency hardening and after hot rolling comprises a range of 24 HRC to 30 HRC, and
wherein the steel is devoid of Cr, Cu, Ni and Al.
2. The method according to claim 1 , wherein a pearlite block size of the steel is 100 μm or less as a circle equivalent diameter.
3. The method according to claim 1 , wherein the steel comprises:
0.45 wt %-0.55 wt % C;
0.21 wt %-0.45 wt % Si
0.50 wt %-1.20 wt % Mn; and
0.15 wt %-0.25 wt % Mo.
4. The method according to claim 1 , wherein a ferrite area ratio is 40% or less before high frequency hardening.
5. The method according to claim 1 , wherein an old austenite crystal grain size in a hardened layer is 8 or more in view of grain size number.
6. The method according to claim 1 , wherein a surface hardness of said steel after said high frequency hardening comprises 650 HV or more.