Treating agent for forming a protective coating and metallic materials with a protective coating
View Patent ↗A protective coating is formed on a metallic material surface by applying a treating agent comprising water, an alkali silicate, and, optionally, a lubricating component to the surface and drying the treating agent. The coating film thereby formed has excellent anti-galling and rust preventive properties. If a lubricating component is present, the coating film also has excellent self-lubricating properties.
1. A treating agent for forming a protective coating, comprising:
an alkali silicate, as represented by the formula M 2 O.nSiO 2 [where n represents a number of 2 to 9, and M represents at least one of Na, K, Li, and NR 4 (where R independently represents a hydrogen atom or an alkyl group)] in an amount of 15-95 mass % based on the total mass of alkali silicate and lubricating component;
at least one lubricating component selected from among soaps, metallic soaps, waxes, and polytetrafluoroethylenes in an amount of 5-85 mass % based on the total mass of alkali silicate and lubricating component;
at least one viscosity modifier in an amount of 1 to 10 wt % based on the total mass of alkali silicate and lubricating component;
and water;
wherein the at least one viscosity modifier comprises at least one inorganic thickener selected from the group consisting of finely powdered silica, bentonite, kaolin, and synthetic hectorite.
2. A treating agent for forming a protective coating according to claim 1 , wherein the alkali silicate is at least one selected from the group consisting of sodium silicates and potassium silicates with SiO 2 /M 2 O molar ratios of 2 to 4, lithium silicates with SiO 2 /M 2 O molar ratios of 3.5 to 8.5, and ammonium silicates with SiO 2 /M 2 molar ratios of 3 to 9.
3. A treating agent for forming a protective coating according to claim 1 , comprising at least one soap selected from the group consisting of sodium stearate and potassium stearate.
4. A treating agent for forming a protective coating according to claim 1 , comprising at least one metallic soap selected from the group consisting of calcium stearate, aluminum stearate, barium stearate, lithium stearate, and zinc stearate.
5. A treating agent for forming a protective coating according to claim 1 , comprising at least one wax selected from the group consisting of polyethylene wax, polypropylene wax, carnauba wax, beeswax, and paraffin wax.
6. A treating agent for forming a protective coating according to claim 1 , wherein the at least one viscosity modifier further comprises organic polymer-based thickeners.
7. A treating agent for forming a protective coating according to claim 1 , wherein the at least one viscosity modifier further comprises at least one organic polymer-based thickener selected from the group consisting of hydroxyethylcellulose, carboxymethylcellulose, polyacrylamide, sodium polyacrylate, polyvinylpyrrolidone, and polyvinyl alcohol.
8. A treating agent for forming a protective coating according to claim 1 , additionally comprising at least one substance selected from the group consisting of solid lubricants and extreme-pressure additives.
9. A treating agent for forming a protective coating, comprising:
an alkali silicate, as represented by the formula M 2 O.nSiO 2 [where n represents a number of 2 to 9, and M represents at least one of Na, K, Li, and NR 4 (where R independently represents a hydrogen atom or an alkyl group)];
at least one lubricating component selected from among soaps, metallic soaps, waxes, and polytetrafluoroethylenes;
at least one viscosity modifier in an amount of 1 to 10 wt % based on the total mass of alkali silicate and lubricating component;
and water;
wherein the at least one viscosity modifier is synthetic hectorite.
10. A treating agent for forming a protective coating, comprising at least alkali silicate selected from the group consisting of sodium silicates and potassium silicates with SiO 2 /M 2 O molar ratios of 2 to 4, lithium silicates with SiO 2 /M 2 O molar ratios of 3.5 to 8.5, and ammonium silicates with SiO 2 /M 2 O molar ratios of 3 to 9, at least one lubricating component in dispersed, emulsified, or both dispersed and emulsified form selected from among soaps, metallic soaps, waxes, and polytetrafluoroethylenes, at least one viscosity modifier in an amount of 1 to 10 wt % based on the total mass of alkali silicate and lubricating component, said at least one viscosity modifier comprising at least one inorganic thickener selected from the group consisting of finely powdered silica, bentonite, kaolin, and synthetic hectorite; and water and wherein the amount of alkali silicate is 50 to 95 mass % and the amount of lubricating component is 5 to 50 mass % on the basis of the total mass of alkali silicate and lubricating component.
11. A treating agent for forming a protective coating according to claim 10 , wherein the alkali silicate is at least one selected from the group consisting of sodium silicates and potassium silicates with SiO 2 /M 2 O molar ratios of 2 to 4.
12. A treating agent for forming a protective coating according to claim 10 , comprising at least one soap selected from the group consisting of sodium stearate and potassium stearate.
13. A treating agent for forming a protective coating according to claim 10 , comprising at least one metallic soap selected from the group consisting of calcium stearate, aluminum stearate, barium stearate, lithium stearate, and zinc stearate.
14. A treating agent for forming a protective coating according to claim 10 , comprising at least one wax selected from the group consisting of polyethylene wax, polypropylene wax, carnauba wax, beeswax, and paraffin wax.
15. A treating agent for forming a protective coating according to claim 10 , wherein the at least one viscosity modifier further comprises organic polymer-based thickeners.
16. A treating agent for forming a protective coating according to claim 10 , wherein the at least one viscosity modifier further comprises at least one organic polymer-based thickener selected from the group consisting of hydroxyethylcellulose, carboxymethylcellulose, polyacrylamide, sodium polyacrylate, polyvinylpyrrolidone, and polyvinyl alcohol.
17. A treating agent for forming a protective coating according to claim 10 , wherein the at least one inorganic thickener is synthetic hectorite.
18. A treating agent for forming a protective coating according to claim 10 , additionally comprising at least one substance selected from the group consisting of solid lubricants and extreme-pressure additives.
19. A treating agent for forming a protective coating according to claim 11 , further comprising:
a viscosity modifier selected from hydroxyethylcellulose and carboxymethylcellulose in an amount of 2 to 5 wt % based on the total mass of alkali silicate and lubricating component; and
at least one solid lubricant and/or extreme-pressure additive, wherein said solid lubricant is selected from the group consisting of graphite, molybdenum disulfide, boron nitride, fluorinated graphite, and mica and said extreme-pressure additive is selected from the group consisting of an olefin sulfide, a sulfide ester, a sulfite, a thiocarbonate a chlorinated fatty acid, a phosphate ester, a phosphite ester, molybdenum dithiocarbamate, molybdenum dithiophosphate, and zinc dithiophosphate.
20. A composition for forming a corrosion preventive protective coating, comprising:
an alkali silicate, as represented by the formula M 2 O.nSiO 2 , where n represents a number of 2 to 9, and M represents at least one of Na, K, Li, and NR 4 , where R independently represents a hydrogen atom or an alkyl group in an amount of 15-95 mass % based on the total mass of alkali silicate and lubricating component;
at least one lubricating component, in an amount of 5 to 85 wt % based on the total mass of alkali silicate and lubricating component, selected from among oils, soaps, metallic soaps, waxes, and polytetrafluoroethylenes;
at least one viscosity modifier in an amount of 1 to 10 wt % based on the total mass of alkali silicate and lubricating component; and
water;
wherein the at least one viscosity modifier comprises at least one inorganic thickener selected from the group consisting of finely powdered silica, bentonite, kaolin, and synthetic hectorite.
21. A composition for forming a corrosion preventive protective coating according to claim 20 , comprising at least one organic polymer-based thickener selected from the group consisting of hydroxyethylcellulose, carboxymethylcellulose, polyacrylamide, sodium polyacrylate, polyvinylpyrrolidone, and polyvinyl alcohol.
22. A composition for forming a corrosion preventive protective coating according to claim 20 , wherein the at least one inorganic thickener is synthetic hectorite.
23. A composition for forming a corrosion preventive protective coating according to claim 20 , additionally comprising at least one substance selected from the group consisting of solid lubricants and extreme-pressure additives.
24. A composition for forming a corrosion preventive protective coating according to claim 20 , wherein the alkali silicate is at least one selected from the group consisting of sodium silicates and potassium silicates with SiO 2 /M 2 O molar ratios of 2 to 4.
25. A composition for forming a corrosion preventive protective coating according to claim 24 , wherein the at least one lubricating component is selected from among oils, soaps, metallic soaps, and waxes.
26. A composition for forming a corrosion preventive protective coating according to claim 25 , wherein the at least one lubricating component is selected from among soaps, metallic soaps, and waxes.