Carbon containing silicon oxide film having high ashing tolerance and adhesion
View Patent ↗An insulating film used for an interlayer insulating film of a semiconductor device and having a low dielectric constant. The insulating film comprises a carbon containing silicon oxide (SiOCH) film which has Si—CH2 bond therein. The proportion of Si—CH2 bond (1360 cm−1) to Si—CH3 bond (1270 cm−1) in the insulating film is preferably in a range from 0.03 to 0.05 measured as a peak height ratio of FTIR spectrum. The insulating film according to the present invention has higher ashing tolerance and improved adhesion to SiO2 film, when compared with the conventional SiOCH film which only has CH3 group.
1. An insulating film comprising;
a carbon containing silicon oxide (SiOCH) film which has Si—CH2 bond in the carbon containing silicon oxide film;
wherein the proportion of Si—CH2 bond (1360 cm−1) to Si—CH3 bond (1270 cm−1) in the insulating film is in a range from 0.03 to 0.05 measured as a peak height ratio of FTIR spectrum.
2. An insulating film as set forth in claim 1 , wherein the relative dielectric constant of the insulating film is equal to or lower than 3.1.
3. An insulating film as set forth in claim 1 , wherein the carbon containing silicon oxide (SiOCH) film is formed by using plasma enhanced CVD process.
4. An insulating film as set forth in claim 1 , wherein the carbon containing silicon oxide (SiOCH) film comprises methylsilsesquioxane.
5. A semiconductor device having an interlayer insulating film formed on or over a semiconductor substrate and a metal wiring conductor which is formed by filling a wiring trench formed in the interlayer insulating film with Cu containing metal via a barrier metal, wherein the interlayer insulating film includes the insulating film comprising:
a carbon containing silicon oxide (SiOCH) film which has Si—CH2 bond in the carbon containing silicon oxide film,
wherein the proportion of Si—CH2 bond (1360 cm−1) to Si—CH3 bond (1270 cm−1) in the insulating film is in a range from 0.03 to 0.05 measured as a peak height ratio of FTIR spectrum.
6. A semiconductor device as set forth in claim 5 , wherein the relative dielectric constant of the insulating film is equal to or lower than 3.1.
7. A semiconductor device as set forth in claim 5 , wherein the carbon containing silicon oxide (SiOCH) film is formed by using plasma enhanced CVD process.
8. A semiconductor device as set forth in claim 5 , wherein the carbon containing silicon oxide (SiOCH) film comprises methylsilsesquioxane.
9. A semiconductor device as set forth in claim 5 , wherein, as a portion of the interlayer insulating film, an SiO2 film is formed on the upper layer portion of the insulating film.
10. A semiconductor device as set forth in claim 5 , wherein, as a portion of the interlayer insulating film, an insulating film for preventing metal diffusion is formed on the lower layer portion of the insulating film.
11. A semiconductor device as set forth in claim 5 , wherein the Cu containing metal contains, in addition to Cu, at least one of Si, Al, Ag, W, Mg, Be, Zn, Pd, Cd, Au, Hg, Pt, Zr, Ti, Sn, Ni and Fe.