Method for drying and using swarf in golf balls
View Patent ↗The present invention relates to an apparatus and method for reusing waste material generated during the manufacturing of golf ball cores. More specifically, the present invention relates to a method and apparatus for drying the waste material in order lower its moisture content. In addition, the present invention relates to golf balls and golf ball components that utilize waste material, and in particular swarf.
1. A method of manufacturing a golf ball comprising the steps of:
providing swarf-containing material;
contacting the swarf containing-material with a stream of hot gas for a sufficient amount of time to dry the swarf-containing material to a desired moisture level;
forming at least one of a golf ball core, intermediate layer, or cover with about 0.01 to about 100 weight percent of the swarf-containing material.
2. The method of claim 1 , wherein the swarf-containing material comprises a thermoset material.
3. The method of claim 1 , wherein the step of contacting the swarf-containing material further comprises moving the swarf-containing material to a hopper to be metered and conveying the swarf-containing material to a stream of hot gas that carries the swarf-containing material into a drying chamber having a dust collector to produce dried swarf.
4. The method of claim 3 , wherein the stream of hot gas may flow continuously or periodically through the dust collector and vented out into the atmosphere.
5. The method of claim 3 , wherein the step of conveying further comprises collecting the dried swarf on the surface of the dust collector and conveying the dried swarf to a storage area before using the dried swarf in the manufacture of golf ball components.
6. The method of claim 1 , wherein the stream of hot gas comprises air, an inert gas, or mixtures thereof.
7. The method of claim 6 , wherein the inert gas comprises nitrogen, argon, helium or a mixture thereof.
8. The method of claim 1 , wherein the temperature of the stream of hot gas is between about 30° C. to about 120° C.
9. The method of claim 1 , wherein the stream of hot gas has a flow rate of between about about 100 to about 6000 m 3 /hour.
10. The method of claim 1 , wherein the step of contacting the swarf-containing material comprises contacting the swarf-containing materials with a stream of hot gas for a period of time of about 1 to about 72 hours.
11. The method of claim 10 , wherein the period of time is about 12 to about 48 hours.
12. The method of claim 3 , wherein the dried swarf has a moisture content below about 5.0 weight percent.
13. The method of claim 12 , wherein the dried swarf has a moisture content of below about 0.50 weight percent.