Hydrophobic coatings and methods
View Patent ↗Substrates have a hydrophobic surface coating comprised of the reaction products of methyltrichlorsilane (MTCS) and dimethyldichlorosilane (DMDCS). Most preferably the substrate is glass. An anchor layer is most preferably formed directly onto the glass substrate surface by means of the application of a humidified reaction product of silicon tetrachloride, followed by the vapor-deposition of MTCS as a cross-linking layer. The hydrophobic layer of MTCS and DMDCS may then be applied over the cross-linking layer of MTCS. A capping layer formed of trimethylchlorosilane (TMCS) may then be vapor deposited onto the hydrophobic layer.
1. A substrate having a hydrophobic surface coating comprised of a silicon oxide anchor layer, a hydrophobic layer and a cross-linking layer between the anchor layer and the hydrophobic layer, wherein the hydrophobic layer consists essentially of the humidified simultaneous vapor deposited reaction product of methyltrichlorosilane (MTCS) and dimethyldichlorsilane (DMDCS), and wherein the cross-linking layer consists essentially of the humidified vapor-deposited reaction product of MTCS.
2. The substrate of claim 1 , further comprising a capping layer which covers the hydrophobic layer and which consists essentially of the humidified vapor deposited reaction product of trimethylchlorosilane (TMCS).
3. The substrate of claim 1 , wherein the humidified vapor-deposited reaction product of MTCS of the cross-linking layer consists essentially of polymethylsilsesquioxane (PMSO), and wherein the humidified simultaneous vapor deposited reaction product of MTCS and DMDCS of the hydrophobic layer is cross-linked polydimethylsiloxane (PMDSO).
4. The substrate of claim 1 , wherein the anchor layer exhibits a haze value of less than about 3.0%.
5. The substrate of claim 4 , wherein the anchor layer exhibits a haze value of less than about 2.0%.
6. The substrate of claim 5 , wherein the anchor layer exhibits a haze value of less than about 1.5%.
7. The substrate of claim 1 , wherein the volume ratio of MTCS to DMDCS in the hydrophobic layer is between about 0.15:1 to about 1.75:1.
8. The substrate of claim 7 , wherein the volume ratio of MTCS to DMDCS in the hydrophobic layer is between about 0.75:1 to about 1.25:1.
9. A process for forming a hydrophobic coating on a glass substrate comprising the steps of:
(a) forming an anchor layer by contacting a surface of the substrate to be coated with a silicon tetrachloride vapor for a time sufficient to form a silicon oxide layer on the glass surface;
(b) forming a cross-linking layer over the silicon oxide layer by the humidified vapor deposition of methyltrichlorosilane (MTCS);
(c) forming a hydrophobic layer over the cross-linking layer by the simultaneous vapor deposition of MTCS and dimethyldichlorosilane (DMDCS) for a time sufficient to form a cross-linked layer of polydimethylsiloxane (PDMSO).
10. The process of claim 9 , wherein the volume ratio of MTCS to DMDCS is between about 0.15:1 to about 1.75 :1.
11. The process of claim 10 , wherein the volume ratio of MTCS to DMDCS is between about 0.75:1 to about 1.25: 1.
12. The process of claim 9 , which further comprising the step of vapor depositing a chloroalkylsilane capping layer over the hydrophobic layer.
13. The process of claim 12 , wherein the chloroalkylsilane capping layer consists essentially of trimethylchlorosilane (TMCS).
14. A coated glass substrate made by the process of claim 9 , 10 , 11 , 12 or 13 .