Optically clear high temperature resistant silicone polymers of high refractive index
View Patent ↗A thermally stable polysiloxane composition is a cross-linked product of a Part A composition, of a Part B composition and a catalyst, the Part A composition being a polysiloxane having 60 to 75 percent by weight phenyl groups, the Part B composition being a polysiloxane having 50 to 80 percent by weight phenyl groups. The composition has the properties of optical clarity as measured by 90% or greater transmission of light of 400 nm wavelength in a 1.0 centimeter path, a refractive index at 589 nm of 1.545 or greater and still has 90% or greater transmission of light of 400 nm wavelength in a 1.0 centimeter path after exposure to 150° C. for 6 hours. The composition is well suited for application as an optically transmissive cover or lens for light emitting diodes and for use in other optical and related devices.
1. A thermally stable polysiloxane composition which is a cross-linked product of a Part A composition, of a Part B composition and of a Part C composition comprising a catalyst that catalyzes the cross-linking of Part A with Part B,
the Part A composition comprising a polysiloxane having 60 to 75 percent by weight phenyl groups;
the Part B composition comprising a polysiloxane having 50 to 80 percent by weight phenyl groups;
the polysiloxane composition having the properties:
(1) of optical clarity as measured by 90% or greater transmission of light of 400 nm wavelength in a 1.0 centimeter path;
(2) thermal stability in that the composition still has 90% or greater transmission of light of 400 nm wavelength in a 1.0 centimeter path after exposure to 150° C. for 6 hours, and
(3) refractive index at 589 nm of 1.545 or greater, and
wherein Part A is a copolymer including methylphenylvinyl-Si—O 1/2 , diphenyl-Si—O, methylvinyl-Si—O and pheny-Si—O 3/2 units, and where Part B is a copolymer including dimethylHydrido-Si—O 1/2 units, diphenyl-Si—O units, phenyl-Si—O 3/2 units, and where the composition includes covalent cross-linked bonds between Part A and Part B, the cross-links having been formed between vinyl and hydride containing units.
2. A polysiloxane composition in accordance with claim 1 comprising 40 to 200 parts by weight of the Part B copolymer for each 100 parts by weight of the Part A copolymer.
3. A polysiloxane composition in accordance with claim 2 that is a gel.
4. A polysiloxane composition in accordance with claim 2 that has a Durometer Type A hardness in the range of 5 to 95.