Vulcanization of dip-molded rubber articles with molten media baths
View Patent ↗Pore-free rubber articles are prepared by dip-molding in a dipping medium that includes a vulcanizing agent, then by immersing the dip former in a heated liquid bath that is chemically inert. A particularly effective liquid bath is molten inorganic salt. In addition, the tensile properties of an article of vulcanized rubber can be improved to an unusually effective degree by immersing the already vulcanized article in a solution of a vulcanizing agent to cause the rubber of the article to absorb or imbibe the vulcanizing agent from the solution, and then immersing the rubber and the imbibed vulcanizing agent in a heated liquid bath to increase the degree of vulcanization.
1. A dip-molded article of a rubber that is substantially pore-free, formed by a process comprising:
(a) dipping a forming member in a latex comprising
(i) a rubber-forming substance and
(ii) a vulcanizing agent, said forming member having an outer surface with a contour complementary to that of said article;
(b) withdrawing said forming member from said latex in such a manner as to leave a film of said latex over said outer surface;
(c) immersing said forming member with said latex thereon in a chemically inert liquid bath at a temperature and for a period of time sufficient to cause vulcanization of said rubber-forming substance by said vulcanizing agent; and
(d) withdrawing said forming member from said liquid bath and separating said substantially pore-free article of rubber from said forming member.
2. A dip-molded article in accordance with claim 1 in which said liquid bath of step (c) is a member selected from the group consisting of molten inorganic salts, oils, glycols, liquefied metals, and brine solutions.
3. A dip-molded article in accordance with claim 1 in which said liquid bath of step (c) is a member selected from the group consisting of molten inorganic salts, silicone oils, and glycols.
4. A dip-molded article in accordance with claim 1 in which said liquid bath of step (c) is a member selected from the group consisting of molten inorganic salts and mixtures thereof.
5. A dip-molded article in accordance with claim 4 in which said molten inorganic salts are members selected from the group consisting of nitrates, nitrites, carbonates, sulfates, phosphates, and halides of potassium, sodium, and lithium.
6. A dip-molded article in accordance with claim 1 in which said temperature of step (c) is from about 100° C. to about 350° C.
7. A dip-molded article in accordance with claim 1 in which said vulcanizing agent is a member selected from the group consisting of organic peroxides, sulfur-containing compounds, selenium-containing compounds, and tellurium-containing compounds.
8. A dip-molded article in accordance with claim 1 in which said vulcanizing agent is a member selected from the group consisting of diacyl peroxides, peroxyketals, dialkyl peroxides, mercaptothiazoles, thiuram sulfides, thiuram disulfides, guanidines, zinc dialkyl dithiocarbamates, selenium dialkyl dithiocarbamates, sodium diethyldithiocarbamate, potassium diethyldithiocarbamate, alkyl phenol sulfides, sulfur-containing polymers, and benzothiazyl disulfide.
9. A dip-molded article in accordance with claim 1 in which said vulcanizing agent is an organic peroxide.
10. A dip-molded article in accordance with claim 1 in which said vulcanizing agent is dicumyl peroxide.
11. A dip-molded article in accordance with claim 1 in which said rubber-forming substance of step (a) is not vulcanized prior to step (a).
12. A dip-molded article in accordance with claim 1 in which said rubber-forming substance is partially vulcanized prior to step (a).
13. A dip-molded article in accordance with claim 12 in which said rubber-forming substance is partially vulcanized prior to step (a) by high energy irradiation.