Coating silicon pellets with dopant for addition of dopant in crystal growth
View Patent ↗An inexpensive method of coating silicon shot with boron atoms comprises (1) immersing silicon shot in an aqueous solution comprising a boric acid and polyvinyl alcohol, and (2) heating the solution so as to evaporate water and form a polymerized polyvinyl alcohol coating containing boron on the shot. A precise amount of this coated shot may then be mixed with a measured quantity of intrinsic silicon pellets and the resulting mixture may then be melted to provide a boron-doped silicon melt for use in growing p-type silicon bodies that can be converted to substrates for photovoltaic solar cells.
1. Method of coating silicon pellets with a selected dopant for use in adding that dopant to a silicon melt comprising the steps of:
forming an aqueous solution comprising a compound containing a selected dopant and polyvinyl alcohol;
combining said aqueous solution with a measured quantity of silicon pellets in a container so as to form a mixture thereof;
heating said mixture to a temperature at which the aqueous solution evaporates and the polyvinyl alcohol polymerizes, whereby the pellets are coated with a dopant-containing coating of polymerized polyvinyl alcohol; and
discontinuing the heating after the dopant-containing coating of polymerized polyvinyl alcohol is dry and the coated silicon pellets are free-flowing.
2. Method according to claim 1 wherein the dopant is boron, phosphorus or arsenic.
3. Method according to claim 1 wherein said compound contains boron.
4. Method of coating silicon pellets with boron dopant for use in adding boron dopant to a silicon melt comprising the steps of:
forming an aqueous solution comprising a compound containing boric acid and polyvinyl alcohol;
combining said aqueous solution with a measured quantity of silicon pellets in a container so as to form a mixture thereof;
heating said mixture to a temperature at which the aqueous solution evaporates and the polyvinyl alcohol polymerizes, whereby the pellets are coated with a boron-containing coating of polymerized polyvinyl alcohol; and
discontinuing the heating after the boron-containing coating of polymerized polyvinyl alcohol is dry and the coated silicon pellets are free-flowing.
5. Method according to claim 4 wherein the pellets are subjected to continued movement in the mixture as it is being heated.
6. Method according to claim 4 wherein said solution has a pH of between about 8 and about 9.
7. Method according to claim 4 wherein said solution also comprises sodium hydroxide.
8. Method according to claim 4 wherein said pellets have an average diameter in the range of about 0.5 to about 0.6 mm.
9. Method of adding boron dopant to a silicon feedstock comprising adding a predetermined amount of silicon pellets coated according to the method of claim 1 to a predetermined quantity of intrinsic silicon pellets, and mixing said coated silicon pellets and said intrinsic silicon pellets so that said coated silicon pellets are dispersed uniformly throughout said quantity of intrinsic silicon pellets.
10. Method of claim 9 wherein said predetermined amount of coated silicon pellets and said predetermined quantity of intrinsic silicon pellets are such as to provide a concentration of boron that will provide a resistivity of approximately 2 to 4 ohm-cm in silicon bodies that are grown from a melt formed by melting said boron-doped and said intrinsic silicon pellets.
11. Method according to claim 9 wherein said boron-doped pellets have an average diameter of between about 0.5 and about 0.6 mm and said intrinsic silicon pellets have an average diameter of about 2.0 mm.
12. Method of coating silicon shot with boron dopant for use in adding dopant to a silicon melt comprising the steps of:
combining in a container (1) a solution comprising boric acid and polyvinyl alcohol having a pH of between about 8 and about 9 and (2) a measured quantity of clean silicon pellets so as to form a mixture thereof;
heating said mixture to a temperature sufficient to removal of the solution by evaporation;
moving the pellets as they are being heated so as to prevent agglomeration thereof; and
terminating the heating after the solution has been fully evaporated and the pellets are dry and free moving.
13. Method according to claim 12 wherein said solution contains sodium hydroxide, potassium hydroxide or ammonium hydroxide.
14. Method according to claim 12 wherein said silicon shot has an average diameter of between about 0.5 and about 0.6 mm.
15. Method of producing a silicon melt comprising:
producing coated silicon pellets according to the method of claim 1 ;
combining a selected quantity of said coated silicon pellets with a measured quantity of intrinsic silicon feedstock in particle form so as to form a mixture of said coated silicon pellets and said silicon feedstock, and
heating said mixture to form a silicon melt.
16. Silicon pellets having a coating comprising polymerized PVA and a selected dopant from the class consisting of boron, phosphorus and arsenic.