High capacitance niobium powders and electrolytic capacitor anodes
View Patent ↗A niobium powder is described which when formed into an electrolytic capacitor anode, the anode has the capacitance of at least 62,000 CV/g. Methods of making flaked niobium powder which have high capacitance capability when formed into electrolytic capacitor anodes is also described. Besides niobium, the present invention is also applicable to other metals, including valve metals.
1. Agglomerated niobium powder characterized by a capacitance of at least 65,000 CV/g and a DC leakage of less than 5.0 nA/CV when the agglomerated niobium powder is tested under electrical properties test conditions of sintering at a temperature of 1100° C. for 10 minutes and anodizing at a formation voltage of 20 Vf at 60° C.
2. The niobium powder of claim 1 , wherein said capacitance is from 65,000 to about 150,000 CV/g.
3. The niobium powder of claim 1 , wherein said capacitance is from about 75,000 to about 175,000 CV/g.
4. The niobium powder of claim 1 , wherein said capacitance is from about 100,000 to about 250,000 CV/g.
5. The niobium powder of claim 1 , wherein said capacitance is from about 125,000 to about 250,000 CV/g.
6. The niobium powder of claim 1 , wherein said capacitance is from about 100,000 to about 210,000 CV/g.
7. The niobium powder of claim 1 , wherein said DC leakage is from about 0.50 nA/CV to less than 5.0 nA/CV.
8. The niobium powder of claim 1 , wherein said niobium powder comprises flaked niobium powder.
9. The niobium powder of claim 1 , wherein said niobium powder has a BET surface area of at least about 5.5 m 2 /g.
10. The niobium powder of claim 1 , wherein said niobium powder has a BET surface area of at least about 7.0 m 2 /g.
11. The niobium powder of claim 1 , wherein said niobium powder has a BET surface area of at least about 10 m 2 /g.
12. The niobium powder of claim 1 , wherein said niobium powder has a BET surface area of from 6.0 m 2 /g to about 12 m 2 /g.
13. The niobium powder of claim 1 , wherein said niobium powder has an oxygen content of less than 1,000 ppm.
14. The niobium powder of claim 1 , wherein said niobium powder has an oxygen content of from about 2,000 ppm to about 60,000 ppm.
15. The niobium powder of claim 1 , wherein said niobium powder is nitrogen doped.
16. The niobium powder of claim 1 , wherein said niobium powder has at least about 100 ppm of nitrogen present.
17. The niobium powder of claim 1 , wherein said niobium powder has nitrogen present in an amount of from about 100 ppm to about 5,000 ppm.
18. The niobium powder of claim 1 , wherein said niobium powder has a flow of at least about 80 mg/s.
19. The niobium powder of claim 1 , wherein said niobium powder has a flow of from about 80 to about 500 mg/s.
20. The niobium powder of claim 1 , wherein said niobium powder has a Scott Density of about 35 g/in 3 or less.
21. The niobium powder of claim 1 , wherein said niobium powder has a Scott Density of from about 10 to about 35 g/in 3 .
22. The niobium powder of claim 1 , wherein said niobium powder has a particle size of from 5 to 80 microns.
23. The niobium powder of claim 1 , wherein said niobium powder has an aspect ratio of from about 3 to about 300.
24. The niobium powder of claim 1 , wherein said niobium powder has a Scott Density of about 35 g/in 3 or less, and a flow of at least about 80 mg/s.
25. The niobium powder of claim 24 , wherein said niobium powder has a particle size of from 5 to 80 microns.
26. The niobium powder of claim 25 , wherein said niobium powder has an aspect ratio of from about 3 to about 300.
27. The niobium powder of claim 25 , wherein said niobium powder is agglomerated.
28. Agglomerated niobium powder characterized by a capacitance of at least 65,000 CV/g and a DC leakage of less than 5.0 nA/CV when the agglomerated niobium powder is tested under electrical properties test conditions of sintering at a temperature of 1100° C. for 10 minutes and anodizing at a formation voltage of 35 Vf at 60° C.