Method of manufacturing an endodontic instrument
View Patent ↗Method for manufacturing endodontic instruments having either helical or non-helical flutes with hard surfaces and resilient cutting edges by either an EDM or ECM process, wherein material is removed from the instrument blank in the desired flute pattern. The EDM or ECM process disintegrates the surface material, and as it cools, at least a portion of the removed material re-deposits onto the surface being machined to form a recast layer having a surface hardness that is at least about 15% greater than the hardness of the material forming the instrument blank.
1. A method for forming an endodontic instrument comprising:
providing an instrument blank with an initial diameter and made of a starting material having a first hardness;
removing starting material from the instrument blank by a method selected from the group consisting of electrical discharge machining, wire electrical discharge machining, electrical discharge grinding and electrochemical machining to form a plurality of cutting edges and flutes having a non-directional surface finish,
wherein at least about 25% of the initial diameter of the instrument blank is removed at a point of maximum metal removal, and
redepositing at least a portion of the removed starting material on the cutting edges and flutes being formed to form a layer of recast material having a second hardness of at least about 15% greater than the first hardness.
2. The method of claim 1 further comprising forming the instrument blank from a wire of the starting material to a pre-determined cross-sectional shape by a method selected from the group consisting of electrical discharge machining, wire electrical discharge machining, electrical discharge grinding and electrochemical machining.
3. The method of claim 1 further comprising twisting the instrument blank having the plurality of flutes to form a plurality of helical flutes.
4. The method of claim 1 wherein the starting material is a superelastic material.
5. The method of claim 4 wherein the superelastic material is a nickel-titanium alloy.
6. The method of claim 5 wherein the nickel-titanium alloy comprises at least about 40 at. % titanium.
7. The method of claim 6 wherein the nickel-titanium alloy further comprises an element selected from the group consisting of: niobium, copper, iron, chromium, cobalt, vanadium, hafnium and palladium.
8. The method of claim 1 wherein the starting material is stainless steel.
9. The method of claim 1 wherein the starting material is a steel alloy.
10. The method of claim 1 wherein removing starting material to form the plurality of flutes includes:
(a) rotating the instrument blank about it's center longitudinal axis while advancing the instrument blank past an electrode without direct contact to remove the starting material thereby forming a first of the plurality of flutes extending helically around the center longitudinal axis of the instrument blank, then
(b) rotatably indexing the instrument blank about the center longitudinal axis not more than 180 degrees and repeating step (a) thereby forming a second of the plurality of flutes extending helically around the center longitudinal axis of the instrument blank.
11. The method of claim 10 further comprising:
(c) repeating step (b) a desired number of times to form a desired number of flutes.
12. The method of claim 10 comprising holding the electrode stationary while advancing the instrument past the electrode.
13. The method of claim 10 comprising rotating the electrode while advancing the instrument past the electrode.
14. The method of claim 10 wherein the instrument blank is advanced past the electrode at a rate of between about 0.025 and about 4 inches per minute.
15. The method of claim 1 wherein removing starting material to form the plurality of flutes includes:
(a) holding the instrument blank stationary while advancing an electrode past the instrument blank without direct contact to remove the starting material thereby forming a first of the plurality of flutes extending non-helically along the center longitudinal axis of the instrument blank, then
(b) rotatably indexing the instrument blank about the center longitudinal axis not more than 180 degrees and repeating step (a) thereby forming a second of the plurality of flutes extending in axial alignment with the first of the plurality of flutes.
16. The method of claim 15 further comprising:
(c) repeating step (b) a desired number of times to form a desired number of flutes.
17. The method of claim 15 wherein the electrode is advanced past the instrument blank at a rate of between about 0.25 and about 4 inches per minute.
18. The method of claim 1 further comprising providing a surface pattern on the electrode whereby a reverse image of the surface pattern is produced on the instrument blank as the starting material is being removed.
19. A method for forming an endodontic instrument comprising the steps of:
forming a wire into an instrument blank with an initial diameter and made of a starting material initially having a first hardness;
forming a first helical flute in the instrument blank by a method selected from the group consisting of electrical discharge machining, wire electrical discharge machining, electrical discharge grinding and electrochemical machining, including rotating the instrument blank about it's center longitudinal axis while advancing the instrument blank axially past an electrode without direct contact with the instrument blank to remove starting material therefrom and thereby form the first helical flute therein, wherein at least about 25% of the initial diameter of the instrument blank is removed at a point of maximum metal removal, and to redeposit at least a portion of the removed starting material on the flute being formed to form a layer of recast material having a non-directional surface finish and a second hardness at least about 15% greater than the first hardness; and
rotatably indexing the instrument blank about the center longitudinal axis not more than 180 degrees and repeating the forming step to form a second helical flute having a non-directional surface finish and the second hardness at least about 15% greater than the first hardness.
20. The method of claim 19 further comprising repeating the indexing step a desired number of times to form a desired number of helical flutes.
21. The method of claim 19 wherein the instrument blank is formed from a wire of the starting material to a pre-determined cross-sectional shape by a method selected from the group consisting of electrical discharge machining, wire electrical discharge machining, electrical discharge grinding and electrochemical machining.
22. The method of claim 19 wherein the starting material is a superelastic material.
23. The method of claim 19 wherein the superelastic material is a nickel-titanium alloy.
24. The method of claim 23 wherein the nickel-titanium alloy comprises at least about 40 at.% titanium.
25. The method of claim 24 wherein the nickel-titanium alloy further comprises an element selected from the group consisting of: niobium, copper, iron, chromium, cobalt, vanadium, hafnium and palladium.
26. The method of claim 19 wherein the starting material is stainless steel.
27. The method of claim 19 wherein the starting material is a steel alloy.
28. The method of claim 19 comprising holding the electrode stationary while advancing the instrument past the electrode.
29. The method of claim 19 comprising rotating the electrode while advancing the instrument past the electrode.
30. The method of claim 19 wherein the instrument blank is advanced past the electrode at a rate of between about 0.25 and about 4 inches per minute.
31. The method of claim 19 further comprising providing a surface pattern on the electrode whereby a reverse image of the surface pattern is produced on the instrument blank as the material is being removed.
32. A method for forming an endodontic instrument comprising the steps of:
forming a wire into an instrument blank with an initial diameter and made of a starting material initially having a first hardness;
forming a first non-helical flute in the instrument blank by a method selected from the group consisting of electrical discharge machining, wire electrical discharge machining, electrical discharge grinding and electrochemical machining, including holding the instrument blank stationary about it's center longitudinal axis while advancing an electrode axially past the instrument blank without direct contact with the instrument blank to remove starting material therefrom and thereby form the first non-helical flute therein, wherein at least about 25% of the initial diameter of the instrument blank is removed at a point of maximum metal removal, and to redeposit at least a portion of the removed starting material on the flute being formed to form a layer of recast material having a non-directional surface finish and a second hardness at least about 15% greater than the first hardness; and
rotatably indexing the instrument blank about the center longitudinal axis not more than 180 degrees and repeating the forming step to form a second non-helical flute extending in axial alignment with the first non-helical flute, the second non-helical flute having a non-directional surface finish and a second hardness at least about 15% greater than the first hardness.
33. The method of claim 32 further comprising repeating the indexing step a desired number of times to form a desired number of non-helical flutes.
34. The method of claim 32 wherein the instrument blank is formed from a wire of the starting material to a pre-determined cross-sectional shape by a method selected from the group consisting of electrical discharge machining, wire electrical discharge machining, electrical discharge grinding and electrochemical machining.
35. The method of claim 32 wherein the starting material is a superelastic material.
36. The method of claim 35 wherein the superelastic material is a nickel-titanium alloy.
37. The method of claim 36 wherein the nickel-titanium alloy comprises at least about 40 at. % titanium.
38. The method of claim 37 wherein the nickel-titanium alloy further comprises niobium.
39. The method of claim 32 wherein the starting material is stainless steel.
40. The method of claim 32 wherein the starting material is a steel alloy.
41. The method of claim 32 wherein the electrode is advanced past the instrument blank at a rate of between about 0.25 and about 4 inches per minute.
42. The method of claim 32 further comprising providing a surface pattern on the electrode whereby a reverse image of the surface pattern is produced on the instrument blank as the starting material is being removed.