Polyethylene blends with good contact transparency
View Patent ↗This invention discloses the production and use of a polyethylene composition comprising a metallocene-produced linear low density polyethylene and a multi modal high density polyethylene prepared from either a Ziegler-Natta or a metallocene catalyst system. The resulting polyethylene composition is suitable for preparing articles having improved environmental stress crack resistance, rigidity, contact transparency, gloss as well as good processing capabilities.
1. A process for preparing a polyethylene resin composition having a multimodal molecular weight distribution that comprises the steps of:
(a) providing from 10 to 90 weight percent of a first metallocene-produced linear low density polyethylene (mLLDPE) resin having a density of from 0.920 to 0.940 g/cm 3 and a melt index MI2 of from 0.1 to 10 dg/min;
(b) providing from 90 to 10 weight percent of a second bi- or multi-modal polyethylene resin prepared either with a Ziegler-Natta or with a metallocene catalyst system, said polyethylene having a density ranging from 0.940 to 0.970 g/cm 3 and a melt index MI2 of from 0.05 to 10 dg/min;
(c) physically blending together the first and second polyethylenes to form a polyethylene resin having a multimodal molecular weight distribution, a density ranging from 0.935 to 0.960 g/cm 3 and a MI2 of from 0.2 to 0.9 dg/min.
2. The process according to claim 1 wherein the first mLLDPE has a density of not more than 0.935 g/cm 3 .
3. The process of claim 1 wherein the first mLLDPE has a melt flow index MI 2 of from 0.5 to 5 dg/min.
4. The process according to claim 1 wherein the second polyethylene resin has a bimodal molecular weight distribution.
5. The process according to claim 4 wherein the second polyethylene resin is produced with a Ziegler-Natta catalyst system.
6. The process according to claim 1 wherein the amount of the first mLLDPE is of from 25 to 75 weight percent and the amount of the second polyethylene resin is of from 25 to 75 weight percent.
7. The process according to claim 6 wherein the amount of each polyethylene component in the blend is of about 50 weight percent.
8. The process according to claim 1 wherein the metallocene catalyst component used to prepare the mLLDPE is ethylene bis(4,5,6,7-tetrahydro-1-indenyl) zirconium dichloride.
9. The method of claim 1 wherein the melt index MI 2 of said first polyethylene resin
is greater than the melt index MI 2 of said second polyethylene resin.
10. The method of claim 9 wherein said blended melt polyethylene resin has a density within the range of 0.940-0.950 g/cm 3 .
11. The process of claim 10 wherein said blended polyethylene resin has a density of about 0.945 g/cm 3 .
12. The process of claim 1 wherein said blended polyethylene resin has a melt index MI 2 within the range of 0.4-0.7 dg/min.
13. The process of claim 12 wherein the melt index MI 2 of said blended polyethylene resin is about 0.5 dg/min.