Rubber composition and method of making same
View Patent ↗Process of producing unvulcanized rubber useful for producing vulcanized rubber with improved hysteresis, which comprises mixing a composition comprising unvulcanized rubber, carbon black and xanthogen polysulfide at an elevated temperature in a non-productive stage and composition suitable for producing unvulcanized rubber useful for producing vulcanized rubber with improved hysteresis, which comprises unvulcanized rubber, a filler comprising carbon black and xanthogen polysulfide.
1. The process of producing an unvulcanized rubber masterbatch useful for producing vulcanized rubber with improved hysteresis, which comprises mixing a composition consisting of unvulcanized rubber, carbon black, xanthogen polysulfide, optionally a processing oil, and optionally, one or more fillers, at a temperature of 149° C. or higher in a non-productive stage.
2. The process of claim 1 wherein mixing is carried out at a temperature of at least 160° for at least three minutes.
3. The process of claim 1 wherein mixing is carried out by multiple re-mills.
4. The process of claim 1 wherein at least part of the xanthogen polysulfide is coated on at least part of the carbon black.
5. The process of claim 1 wherein the xanthogen polysulfide comprises xanthogen disulfide having the structure:
wherein R and R 1 are independently alkyl groups.
6. The process of claim 5 wherein the alkyl groups R and R 1 are butyl.
7. The process of claim 1 wherein the xanthogen polysulfide is present in a concentration of 0.1 to 100 parts by weight per 100 parts by weight carbon black.
8. The process of claim 1 wherein said composition comprises silica.
9. A composition suitable for producing unvulcanized rubber useful for producing vulcanized rubber with improved hysteresis, which consists of unvulcanized rubber, carbon black, xanthogen polysulfide, optionally, a processing oil, and optionally, one or more fillers.
10. The composition of claim 9 wherein at least part of the xanthogen polysulfide is coated on at least part of the carbon black.
11. The composition of claim 10 wherein the xanthogen polysulfide comprises xanthogen disulfide having the structure:
wherein R and R 1 are independently alkyl groups.
12. The composition of claim 11 wherein R and R 1 are butyl groups.
13. The composition of claim 10 wherein the xanthogen polysulfide is present in a concentration of 0.5 to 20 parts by weight per 100 parts by weight filler.
14. The composition of claim 13 wherein the one or more fillers is silica.
15. The process of producing vulcanized rubber with improved hysteresis (1) which comprises mixing a composition consisting of unvulcanized rubber, carbon black, xanthogen polysulfide, optionally, a processing oil, and optionally, one or more fillers, at a temperature of 149° C. or higher, in a non-productive mixing step, then (2) adding curative ingredients in subsequent mixing steps and vulcanizing the rubber.
16. The process of claim 15 wherein step (1) is carried out at a temperature of at least 160° C. for at least three minutes.
17. The process of claim 15 wherein at least part of the xanthogen polysulfide is coated on at least part of the carbon black.
18. The process of claim 15 wherein the one or more fillers is silica.