Catalytic coating for the self-cleaning of ovens and stoves
View Patent ↗A part on or in a cooking, roasting, baking, or grilling device with a self-cleaning coating enables remnants of foodstuffs to be removed without mechanical action. The part includes a coating which has a structure comprised of (a) porous particles A, and (b) a binder, in which the porous particles A do not have a solid or liquid secondary phase in their pores (a).
1. A cooking, roasting, baking or grilling device having a substrate with a self-cleaning coating thereon, said coating comprising:
a plurality of particles having first pores therein, wherein spaces between adjacent particles form second pores which allow for solids and liquids to enter therein; and
a binder for binding said particles together at contacts points;
wherein said binder is a colloidal solution comprising one of an inorganic polymer and an inorganic sol, wherein said colloidal solution is formed with at least one of SiO 2 , TiO 2 , Al 2 O 3 , ZrO 2 , SiC, Si 3 N 4 , and B 2 O 3 .
2. The device according to claim 1 , wherein said porous particles are thermally and chemically stable porous metal oxides, carbides or nitrides.
3. The device according to claim 1 , wherein said porous particles are at least one of SiO 2 , TiO 2 , Al 2 O 3 , ZrO 2 , SiC, Si 3 N 4 , C and B 2 O 3 .
4. The device according to claim 1 , wherein said porous particles have a diameter in the range of 5 to 100 microns.
5. The device according to claim 1 , wherein said porous particles have open-cell pores.
6. The device according to claim 1 , wherein said binder comprises particles having a diameter in the range of 0.5 to 10 microns.
7. The device according to claim 1 , wherein said coating includes addition particles that function to at least one of, reduce the roughness of the coating, improve the binding between said porous particles, improve the binding between said coating and the substrate, adjust the color of said coating, or improve the thermal decomposition, the haptics or the spreading ability of said coating.
8. The device according to claim 7 , wherein said additional particles are at least one of nanoscale particles, particles in the micrometer range, pigment particles, and metals.
9. The device according to claim 8 , wherein said additional particles comprise at least one of metal oxides, carbides and nitrides.
10. The device according to claim 1 , wherein the part or portion is a part or portion of a baking oven muffle.
11. The device according to claim 1 , wherein the part or portion is a part or portion of an oven or a stove.
12. The device according to claim 3 , wherein said porous particles are at least one of Al 2 O 3 and SiO 2 .
13. The device according to claim 6 , wherein said particles have a diameter of about 1 to 5 microns.
14. The device according to claim 4 , wherein said diameter is about 10 to 80 microns.
15. The device according to claim 4 , wherein said diameter is about 20 to 60 microns.
16. The device according to claim 4 , wherein said diameter is about 30 to 50 microns.
17. A cooking device having has a substrate with a self-cleaning coating thereon which enables remnants of foodstuffs to be removed without mechanical action, comprising:
the coating having a structure formed from a plurality of porous particles having pores therein and an inorganic binder being temperature resistant up to about 500 degrees C., wherein said inorganic binder includes an inorganic colloidal solution having ZrO 2 particles in liquid phase.
18. The device according to claim 1 , wherein said inorganic polymer is one of a silicone resin and a polymeric phosphate.
19. The device according to claim 1 , wherein said first pores are less than 1 μm in diameter in order to prevent a solid or liquid from entering therein.
20. The device according to claim 1 , wherein said binder forms a membrane surrounding said particles, and said membrane includes pores which are small enough to prevent a solid or liquid from entering therein.
21. The device according to claim 20 , wherein said binder is temperature resistant up to about 500 degrees C.
22. A substrate with a self-cleaning coating thereon, said coating comprising:
a plurality of particles having first pores therein, the particles comprising at least one of a metal oxide, a carbide, and a nitride, wherein spaces between adjacent particles form second pores which are larger than the first pores such that the first pores prevent a solid or liquid from entering therein and the second pores allow for solids and liquids to enter therein; and
a binder for binding said particles together at contacts points, wherein said binder is formed with at least one of a metal oxide, a carbide, and a nitride.
23. A substrate with a self-cleaning coating thereon, said coating comprising:
a plurality of particles having first pores therein, the particles comprising at least one of a metal oxide, a carbide, and a nitride, wherein spaces between adjacent particles form second pores; and
a binder for binding said particles together at contacts points, wherein said binder forms a membrane surrounding said particles, wherein said binder is formed with at least one of a metal oxide, a carbide, and a nitride, and wherein said binder forms third pores which are smaller than the second pores such that the third pores prevent a solid or liquid from entering therein and the second pores allow for solids and liquids to enter therein.