Graphite loaded silicon carbide and methods for making
View Patent ↗The invention provides exemplary silicon carbide ceramic bodies and processes for making such ceramic bodies. In one embodiment, a raw batch for producing a ceramic body includes a silicon carbide slurry and agglomerates of particles defining a dry lubricant mixture. The mixture includes a binder and a dry lubricant such as graphite, with a majority of the agglomerates having a shape that is generally spherical.
1. A method of making a raw batch for producing a composite ceramic body, the method comprising:
preparing a dry lubricant slurry;
preparing a binder;
mixing the dry lubricant slurry and the binder; and
drying the combined dry lubricant slurry and the binder to form a dry mixture having a plurality of agglomerates;
wherein a majority of the plurality of agglomerates have a shape that is generally spherical; and
wherein the binder has a demarcation temperature that is less than the boiling point of water, and wherein the binder is soluble in water that is above the demarcation temperature and insoluble in water that is below the demarcation temperature.
2. The method as in claim 1 further comprising preparing the binder and mixing the dry lubricant slurry and binder at a temperature greater than the demarcation temperature.
3. The method as in claim 1 wherein the dry lubricant slurry comprises a graphite.
4. The method as in claim 1 further comprising mixing the dry mixture with a silicon carbide precursor slurry at a temperature that is below the demarcation temperature.
5. A method of making a ceramic component, the method comprising:
preparing a dry lubricant mixture, the dry lubricant mixture comprising:
a dry lubricant; and
a binder, the binder having a demarcation temperature, and wherein the binder is soluble in water that is above the demarcation temperature and insoluble in water that is below the demarcation temperature; and
combining the dry lubricant mixture with a silicon carbide precursor slurry;
wherein the preparing the dry lubricant mixture occurs at a temperature above the demarcation temperature, and the combining of the dry lubricant mixture with the silicon carbide precursor slurry occurs at a temperature below the demarcation temperature.
6. The method as in claim 5 wherein the dry lubricant mixture comprises a plurality of generally spherical agglomerates having a size between about thirty (30) microns and about one-hundred and twenty (120) microns.
7. The method as in claim 5 wherein the demarcation temperature is a temperature between about eighty-eight degrees Celsius (88° C.) and about ninety degrees Celsius (90° C.).
8. The method as in claim 5 wherein the dry lubricant comprises a graphite, the graphite having an average particle size between about two (2) microns and about seven (7) microns.
9. The method as in claim 5 further comprising drying the combined dry lubricant mixture and silicon carbide precursor slurry, and forming a ceramic body therefrom.
10. The method as in claim 9 wherein forming the ceramic body comprises forming the ceramic body using a green compaction forming technique.
11. The method as in claim 9 wherein the ceramic body is a bearing.
12. The method as in claim 9 wherein the ceramic body is a pump seal.
13. The method as in claim 9 wherein the ceramic body has a generally uniform distribution of dry lubricant inclusions.
14. The method as in claim 13 wherein a majority of the dry lubricant inclusions are generally spherical or ellipsoidal in shape.
15. The method as in claim 13 wherein the dry lubricant inclusions comprise between about two (2) percent and about twelve (12) percent of the ceramic body by volume.
16. The method as in claim 13 wherein the generally uniform distribution of dry lubricant inclusions is substantially free of a lamination effect.
17. The method as in claim 13 wherein the dry lubricant inclusions comprise a graphite.
18. A composite ceramic body, comprising:
silicon carbide in major amount; and
unreacted inclusions of a dry lubricant in minor amount, wherein a majority of the inclusions are substantially spherical or ellipsoidal in shape, the inclusions comprising between about two (2) percent and about twelve (12) percent of the ceramic body by volume;
wherein the inclusions are substantially free of abutting inclusions to prevent a lamination effect in the ceramic body.
19. The composite ceramic body as in claim 18 wherein the majority of the inclusions have a nominal diameter that is less than one-hundred (100) microns.
20. The composite ceramic body as in claim 18 wherein the inclusions of dry lubricant comprise a graphite inclusion.