Methods of forming honeycomb sandwich composite panels
View Patent ↗The invention is to perform operations from sealing of a honeycomb core with a thermosetting sealing material having an adhesive property to its hardening in one step, prevent a resin from flowing into cells of the honeycomb core during resin impregnating operation, and thereby mold low-cost honeycomb sandwich components by using RTM technique which is adopted in molding solid materials, for instance. Dry fabric sheets are stacked on both sides of a honeycomb core with thermosetting sealing members having an adhesive property placed in between, and the sealing members and the dry fabric sheets are heated at the curing temperature of the sealing members to cause initial hardening of the sealing members and to dry the dry fabric sheets. Then, the dry fabric sheets are impregnated with a thermosetting resin and the resin impregnated into the dry fabric sheets is hardened by hot-pressing an entire assembly thus prepared under specific conditions.
1. A method of forming a honeycomb sandwich composite panel by a resin transfer molding process consisting essentially of:
stacking a plurality of thermosetting sealing materials on at least one of sides of a honeycomb; said each of thermosetting sealing materials having an adhesive property, and including one of short fibers of glass and non-woven fabric of glass;
stacking a dry fabric on said thermosetting sealing materials;
hardening said thermosetting sealing materials by heating to a sufficient temperature and maintaining this temperature for a specified period of time;
impregnating the dry fabric with a thermosetting resin; and
hardening said thermosetting resin impregnated into said dry fabric by heating said thermosetting resin and said dry fabric to the curing temperature of said thermosetting resin and hot-pressing them for a specified time period.
2. The method of forming a honeycomb sandwich composite panel according to claim 1 , wherein:
said thermosetting sealing material is a laminate of three layers.
3. The method of forming a honeycomb sandwich composite panel according to claim 1 , wherein:
said thermosetting sealing material is hardened at a temperature lower than the curing temperature of the impregnating resin.
4. The method of forming a honeycomb sandwich composite panel according to claim 1 , wherein:
said curing temperature of said thermosetting sealing material is about 120±5° C., and said specified curing time period is about 130±10 minutes.
5. The method of forming a honeycomb sandwich composite panel according to claim 1 , wherein:
said thermosetting sealing material is hardened by heating at a rate of 1° C. per minute or less.
6. The method of forming a honeycomb sandwich composite panel according to claim 1 , wherein:
said thermosetting sealing material is heated to harden said thermosetting sealing material and to dry said dry fabric simultaneously.
7. The method of forming a honeycomb sandwich composite panel according to claim 1 , wherein:
said thermosetting sealing material is hardened by heating said thermosetting sealing material up to the curing temperature of said thermosetting sealing material.
8. The method of forming a honeycomb sandwich composite panel according to claim 1 , wherein:
said thermosetting sealing material is a resin film including one of said short fibers of glass and said non-woven fabric of glass to adjust viscosity of said resin film having a sufficient sealing effect to prevent said thermosetting resin from flowing into said honeycomb during said impregnating process.
9. A method of forming a honeycomb sandwich composite panel by a resin transfer molding process consisting essentially of:
stacking a thermosetting sealing material on at least one of sides of a honeycomb; said thermosetting sealing material having an adhesive property, and comprising a plurality of epoxy resin adhesive films and an epoxy resin film placed between said plurality of epoxy resin adhesive films, said epoxy resin film including one of short fibers of glass and non-woven fabric of glass;
stacking a dry fabric on said thermosetting sealing material;
hardening said thermosetting sealing material by heating to a sufficient temperature and maintaining this temperature for a specified period of time;
impregnating the dry fabric with a thermosetting resin; and
hardening the resin impregnated into said dry fabric by heating said resin and said fabric to the curing temperature of said thermosetting resin and hot-pressing them for a specified time period.
10. The method of forming a honeycomb sandwich composite panel according to claim 9 , wherein:
said thermosetting sealing material is hardened at a temperature lower than the curing temperature of the impregnating resin.
11. The method of forming a honeycomb sandwich composite panel according to claim 9 , wherein:
said curing temperature of said thermosetting sealing material is about 120±5° C., and said specified curing time period is about 130±10 minutes.
12. The method of forming a honeycomb sandwich composite panel according to claim 9 , wherein:
said thermosetting sealing material is hardened by heating at a rate of 1° C. per minute or less.
13. The method of forming, a honeycomb sandwich composite panel according to claim 9 , wherein:
said thermosetting sealing material is heated to harden said thermosetting sealing material and to dry said dry fabric simultaneously.
14. The method of forming a honeycomb sandwich composite panel according to claim 9 , wherein:
said thermosetting sealing material is hardened by heating said thermosetting sealing material up to the curing temperature of said thermosetting sealing material.
15. The method of forming a honeycomb sandwich composite panel according to claim 9 , wherein:
said epoxy resin film includes one of said short fibers of glass and said non-woven fabric of glass to adjust viscosity of said epoxy resin film having a sufficient sealing effect to prevent said thermosetting resin from flowing into the honeycomb during said impregnating process.