Porous material and method for manufacturing same, and electrochemical element made using this porous material
View Patent ↗Conventional porous carbon materials obtained by carbonizing an organic gel were prone to shrinkage during their manufacture, in the course of which the density rose and the specific surface area decreased. Another problem was that density and specific surface area were difficult to control after an organic gel had already been formed. In the present invention, a carbon material with a large specific surface area is formed by forming a composite porous material having a reticulated skeleton and composed of a dry gel of an inorganic oxide, and taking advantage of the reaction of this dry gel of an inorganic oxide as a structural support. In one method, a carbon material is formed in this reticulated skeleton in a state in which the characteristics of a dry gel of an inorganic oxide with a large specific surface area are maintained. In another method, the specific surface area of a carbon material is further increased by removing the inorganic oxide of the reticulated skeleton in which the carbon material was formed.
1. A method for manufacturing a porous material having a reticulated skeleton in which:
(1) the reticulated skeleton comprises an interior and a surface component;
(2) the surface component includes a carbon material; and
(3) the interior comprises a) empty space, or b) an inorganic oxide and empty space,
wherein the method comprises in the following order:
step 1 of obtaining a carbon precursor-containing wet gel by imparting a carbon precursor to a wet gel of an inorganic oxide having a reticulated skeleton;
step 2 of obtaining a carbon precursor wet gel by removing all or part of the inorganic oxide from the carbon precursor-containing wet gel;
step 3 of obtaining a carbon precursor-containing dry gel by subjecting the carbon precursor wet gel to supercritical drying; and
step 4 of obtaining a carbon-containing porous material by subjecting the carbon precursor-containing dry gel to a carbonization treatment.
2. The manufacturing method according to claim 1 , wherein the carbon precursor comprises an organic polymer.
3. The manufacturing method according to claim 2 , wherein the organic polymer has one or more carbon-carbon unsaturated bonds.
4. The manufacturing method according to claim 2 , wherein the organic polymer has one or more aromatic rings.
5. The manufacturing method according to claim 2 , wherein the organic polymer is at least one member selected from the group consisting of phenol resins, polyimides, and polyacrylonitriles.
6. The manufacturing method according to claim 1 , further comprising a step of supporting a catalyst.