Magnetic recording medium
View Patent ↗The invention provides a magnetic recording medium comprising a support having provided thereon a nonmagnetic layer containing a nonmagnetic powder, and a magnetic layer containing a ferromagnetic powder formed on the nonmagnetic layer after coating and drying thereof, wherein the ferromagnetic layer is a hexagonal ferrite powder having an average tabular diameter of 15 to 40 nm or a ferromagnetic metal powder having an average major axis length of 25 to 100 nm, the thickness of the magnetic layer is from 0.01 to 0.3 μm, the thickness of the nonmagnetic layer is from 0.5 to 5 μm, and the specific surface area and the total pore volume of the magnetic recording medium itself measured by a nitrogen absorption measured method are from 0.1 to 50 m 2 /g and from 0.001 to 1 ml/g, respectively, thereby being to provide the magnetic recording medium for high density recording remarkably improved in electromagnetic characteristics, particularly in high density recording characteristics.
1. A magnetic recording medium comprising a support having provided thereon a nonmagnetic layer containing a nonmagnetic powder and carbon black, and a magnetic layer containing a ferromagnetic metal powder formed on the nonmagnetic layer after coating and drying thereof,
wherein the ferromagnetic metal powder has an average major axis length of 25 to 100 nm, the magnetic layer has a thickness of 0.01 to 0.3 μm, the nonmagnetic layer has a thickness of 0.5 to 5 μm, the carbon black is present in the nonmagnetic layer in an amount of from 5 to 100% by weight, based on the amount of nonmagnetic powder, and the magnetic recording medium has a specific surface area of 0.1 to 50 m 2 /g and a total pore volume of 0.001 to 1 ml/g, the specific surface area and the total pore volume being measured by a nitrogen absorption method.
2. The magnetic recording medium according to claim 1 , which is a magnetic tape having a squareness ratio of 0.7 or more.
3. The magnetic recording medium according to claim 1 , which is capable of being reproduced with Magneto Resistive (MR) Head.
4. A magnetic recording medium obtained by a process comprising the steps of:
coating a nonmagnetic layer containing a nonmagnetic powder and carbon black on a support;
drying the nonmagnetic layer to form a dried nonmagnetic layer; and
coating a magnetic layer containing a ferromagnetic metal powder on the dried nonmagnetic layer;
wherein the ferromagnetic metal powder has an average major axis length of 25 to 100 nm, the magnetic layer has a thickness of 0.01 to 0.3 μm, the nonmagnetic layer has a thickness of 0.5 to 5 μm, the carbon black is present in the nonmagnetic layer in an amount of from 5 to 100% by weight, based on the amount of nonmagnetic powder, and the magnetic recording medium has a specific surface area of 0.1 to 50 m 2 /g and a total pore volume of 0.001 to 1 ml/g, the specific surface area and the total pore volume being measured by a nitrogen absorption method.
5. A method for producing a magnetic recording medium comprising:
coating a nonmagnetic layer containing a nonmagnetic powder and carbon black on a support;
drying the nonmagnetic layer to form a dried nonmagnetic layer; and
coating a magnetic layer containing a ferromagnetic metal powder on the dried nonmagnetic layer;
wherein the ferromagnetic metal powder has an average major axis length of 25 to 100 nm, the magnetic layer has a thickness of 0.01 to 0.3 μm, the nonmagnetic layer has a thickness of 0.5 to 5 μm, the carbon black is present in the nonmagnetic layer in an amount of from 5 to 100% by weight, based on the amount of nonmagnetic powder, and the magnetic recording medium has a specific surface area of 0.1 to 50 m 2 /g and a total pore volume of 0.001 to 1 ml/g, the specific surface area and the total pore volume being measured by a nitrogen absorption method.