Coating solution containing cocrystals and or crystals of a charge-generation pigment or a mixture of charge-generation pigments
View Patent ↗A method for preparing a coating solution containing a cocrystallized titanyl phthalocyanine-titanyl fluorophthalocyanine, the method comprising: dry milling a charge-generation pigment or mixtures of charge-generation pigments; increasing the amorphousness of the pigment mixture as determined by X-ray crystallography using X-radiation characteristic of Cu Kα at a wavelength of 1.541 Å of the Bragg angle 2θ to provide an amorphous pigment mixture; contacting the amorphous pigment mixture with a first organic solvent having a gamma c hydrogen bonding parameter of less than 9, with or without the presence of a dispersant material, to produce a crystalline pigment of the charge-generation pigment prior to contacting the pigment with a second organic solvent having a gamma c hydrogen bonding parameter greater than 9; mixing at least one of a second organic solvent, a dispersant and a binder with the crystalline pigment/first solvent mixture without isolating the crystalline pigment to produce a mixture; and, adjusting the concentrations of the first organic solvent, crystalline pigment, binder, dispersants and second organic solvent as required to produce the coating solution of a selected composition.
1. A method for preparing an electrophotographic element coating solution containing a crystallized charge-generation pigment material, the method comprising:
a) dry milling a crude charge-generation pigment material to produce finely divided amorphous pigment material wherein the crystalline charge-generation pigment material is selected from the group consisting of titanyl phthalocyanine, titanyl fluorophthalocyanine, and mixtures thereof;
b) contacting the amorphous pigment material with a first solvent to produce a finely-divided crystalline charge-generation pigment, optionally in the presence of a dispersant material; and,
c) mixing a binder and a second solvent with the charge-generation crystalline pigment without isolating the crystalline pigment to produce the coating solution, the second solvent being the same or different than the first solvent.
2. The method of claim 1 , wherein the first solvent has a gamma c hydrogen bonding parameter less than 9.
3. The method of claim 1 , wherein said contacting is in the presence of a dispersant material.
4. The method of claim 1 , wherein the gamma hydrogen bonding parameter is less than 8.
5. The method of claim 1 , the gamma c hydrogen bonding parameter is less than 7.
6. The method of claim 3 , wherein the dispersant is selected from the group consisting of substituted ammonium salt of a colored acid wherein from 16 to 60 carbon atoms are contained in at least three chains attached to the nitrogen atom of the substituted ammonium ion, polymeric materials having a plurality of pendant quaternary ammonium salt groups, polyvinyl formal, polyvinyl acetal, polyvinylbutyral and combinations thereof.
7. The method of claim 3 , wherein the dispersant is selected from the group consisting of polyvinyl formal, polyvinyl acetal, polyvinylbutyral.
8. The method of claim 3 , wherein the dispersant is polyvinylbutyral.
9. The method of claim 3 , wherein the dispersant is the sole binder used in the coating solution.
10. The method of claim 3 , wherein the binder is a polyester ionomer.
11. The method of claim 3 , wherein the binder is a polyester ionomer made from isophthalic acid (95 mole), 4-sodio-isophthalic sulfonate (5 mole %), diethylene glycol (20 mole %), and neopentyl glycol (80 mole %).
12. The method of claim 3 , wherein the dispersant is mixed with the amorphous pigment and the first solvent in an amount equal to from about 5 to about 60 weight percent based on total solids in the mixture.
13. The method of claim 12 , wherein the amorphous pigment, the first solvent and the dispersant are wet milled to produce the crystalline pigment.
14. The method of claim 1 , wherein the finely divided crystalline pigment, solvent, binder and dispersant are adjusted to produce a coating solution having a crystalline product content from about 20 to about 80 weight percent based upon the weight of the total solids of the coating solution; a binder content from about 19 to about 65 weight percent based upon the weight of the total solids of the coating solution and a dispersant content from about 1 to about 15 weight percent based upon the weight of the total solids of the coating solution; a solvent content from about 98 to about 80 weight percent based upon the weight of the coating solution.
15. The method of claim 14 , wherein the binder content is from about 40 to about 70 weight percent based upon the total solids in the coating solution.
16. The method of claim 14 , wherein the dispersant content is from about 5 to about 30 weight percent based upon the total solids in the coating solution.
17. The method of claim 1 , wherein the amorphous pigment material, first solvent and dispersant are wet milled to produce finely divided crystallized pigment having a particle size less than about 0.5 micron.
18. The method of claim 1 , wherein the dispersant is mixed with the amorphous pigment and first solvent in an amount equal to from about 40 to about 70 weight percent based on the total solids in the coating solution.
19. The method of claim 18 , wherein the amorphous pigment, the first solvent and the dispersant are wet milled to produce the crystalline pigment.
20. A method for preparing an electrophotographic element coating solution containing a crystallized charge-generation pigment material, the method comprising:
a) dry milling a crude charge-generation pigment material to produce a finely divided amorphous pigment material wherein the crude-generation pigment material is titanyl phthalocyanine, titanyl fluorophthalocyanine, or mixtures thereof;
b) mixing the finely divided amorphous pigment material with a solvent having a gamma hydrogen bonding parameter less than 9, a binder and a dispersant to produce the coating solution containing crystallized pigment material.
21. The method of claim 20 , wherein the pigment material, binder, solvent and dispersant are wet milled to produce the coating solution.
22. The method of claim 20 , wherein the finely divided crystalline pigment, solvent, binder and dispersant are adjusted to produce a coating solution having a crystalline product content from about 20 to about 80 weight percent based upon the weight of the total solids of the coating solution; a binder content from about 19 to about 65 weight percent based upon the weight of the total solids of the coating solution and a dispersant content from about 1 to about 15 weight percent based upon the weight of the total solids of the coating solution; a solvent content from about 98 to about 80 weight percent based upon the weight of the coating solution.
23. The method of claim 20 , wherein a solvent having a gamma c hydrogen bonding parameter greater than 9 is mixed with the pigment material, binder, solvent and dispersant after the pigment material has been wet by, and crystallized in the presence of the solvent having a gamma c hydrogen bonding parameter less than 9.
24. A method for preparing an electrophotographic element coating solution containing a crystallized charge-generation pigment material, the method comprising:
a) dry milling a crude charge-generation pigment material to produce a finely divided amorphous pigment material wherein the crude charge-generation pigment material is titanyl phthalocyanine, titanyl fluorophthalocyanine, or mixtures thereof;
b) mixing the finely divided amorphous pigment material with a solvent having a gammac hydrogen bonding parameter greater than 9, a binder and a dispersant to produce the coating solution containing crystallized pigment material.
25. The method of claim 24 , wherein the pigment material, binder, solvent and dispersant are wet milled to produce the coating solution.