Method for making a polyether monomer
View Patent ↗A method for making a polyether monomer having at least one unsaturated site per molecule and having a desired number of alkoxyl repeating units includes the steps of reacting an active hydrogen-containing monomer having at least one unsaturated site per molecule with an alkyl oxide in the presence of an alkoxylation catalyst and a polymerization inhibitor at a temperature from about 30° C. to less than 45° C. to produce a polyether monomer. In one embodiment, from about 5 to about 1000 parts by weight of a phenothiazine polymerization inhibitor per one million parts by weight of the active hydrogen-containing monomer phenothiazine compound is used as the polymerization inhibitor.
1. A method for making a polyether monomer having at least one unsaturated site per molecule and having a desired number of alkoxyl repeating units per molecule, comprising reacting in the absence of oxygen an active hydrogen-containing monomer having at least one unsaturated site per molecule with an alkyl oxide in the presence of an alkoxylation catalyst and a phenothiazine polymerization inhibitor at a temperature from about 30° C. to less than 45° C. to produce the polyether monomer.
2. The method of claim 1 , wherein the alkylene oxide is one or more of ethylene oxide and propylene oxide.
3. The method of claim 1 , wherein the active hydrogen-containing monomer is one or more of hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxyethyl methacrylate, and hydroxypropyl methacrylate.
4. The method of claim 1 wherein the phenothiazine polymerization inhibitor is phenothiazine.
5. The method of claim 1 wherein the phenothiazine polymerization inhibitor is present in an amount of from about 5 to about 1000 parts by weight per one million parts by weight of the active hydrogen-containing monomer.
6. A method for making a polyalkoxylated acrylic or methacrylic ester, comprising reacting one or more of hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxyethyl methacrylate and hydroxypropyl methacrylate with one or more of ethylene oxide and propylene oxide in the presence of an alkoxylation catalyst and a polymerization inhibitor at a temperature from about 30° C. to less than 45° C.
7. A method for making a stabilized polyether monomer having at least one unsaturated site per molecule and having a desired number of alkoxyl repeating units per molecule, comprising:
reacting an active hydrogen-containing monomer having at least one unsaturated site per molecule with an alkyl oxide in the presence of an alkoxylation catalyst and from about 5 to about 1000 parts by weight of a phenothiazine polymerization inhibitor per one million parts by weight of the active hydrogen-containing monomer to produce the polyether monomer.
8. The method of claim 7 , wherein the alkylene oxide is one or more of ethylene oxide and propylene oxide.
9. The method of claim 7 , wherein the active hydrogen-containing monomer is one or more of hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxyethyl methacrylate, hydroxypropyl methacrylate.
10. The method of claim 7 , wherein the phenothiazine polymerization inhibitor is phenothiazine.
11. The method of claim 7 , wherein less than 1000 parts by weight p-methoxy phenol per one million parts by weight active hydrogen-containing monomer is added to the active hydrogen-containing monomer, alkyl oxide, alkoxylation catalyst, and phenothiazine polymerization inhibitor.
12. A method for making a polyalkoxylated acrylic or methacrylic ester, comprising reacting one or more of hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxyethyl methacrylate, and hydroxypropyl methacrylate with one or more of ethylene oxide and propylene oxide in a substantially inert atmosphere in the substantial absence of oxygen and in the presence of an alkoxylation catalyst and from about 5 to about 1000 parts by weight of a phenothiazine polymerization inhibitor per one million parts by weight of the hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxyethyl methacrylate, and hydroxypropyl methacrylate.
13. A stabilized polyether monomer composition prepared by the method of claim 1 , comprising:
a polyether monomer, said polyether monomer having at least one unsaturated site per molecule and having a desired number of alkoxyl repeating units per molecule, and
an effective amount of a phenothiazine polymerization inhibitor.
14. The composition of claim 13 , wherein the polyether monomer is one or more of a polyethoxyl acrylic ester, a polyethoxyl methacrylic ester, a polypropoxyl acrylic ester, and a polypropoxyl methacrylic ester.
15. The composition of claim 13 , wherein the phenothiazine polymerization inhibitor is phenothiazine.
16. The composition of claim 13 , wherein the composition comprises about 5 to about 300 parts by weight of a phenothiazine polymerization inhibitor per one million parts by weight of the polyether monomer.
17. The polyether monomer of claim 13 , wherein the p-methoxy phenol content of the polyether monomer is less than about 1000 parts by weight p-methoxy phenol per one million parts by weight polyether monomer.
18. A stabilized polyether monomer composition prepared by the method of claim 1 , comprising:
one or more of a polyethoxyl acrylic ester, a polyethoxyl methacrylic ester, a polypropoxyl acrylic ester, and a polypropoxyl methacrylic ester, and
from about 5 to about 300 parts by weight of a phenothiazine polymerization inhibitor per one million parts by weight of the polyether monomer.
19. A method for making a polyether monomer having at least one unsaturated site per molecule and having a desired number of alkoxyl repeating units per molecule, consisting essentially of reacting in the absence of oxygen an active hydrogen-containing monomer having at least one unsaturated site per molecule with an alkyl oxide in the presence of an alkoxylation catalyst and a phenothiazine polymerization inhibitor at a temperature from about 30° C. to less than 45° C. to produce the polyether monomer.
20. The method of claim 1 comprising conducting the reaction in the absence of solvent.