Surface treatment process for implants made of titanium alloy
View Patent ↗A titanium 6 A1/4V alloy is provided with a surface topography that is similar to the Osseotite® surface produced on commercially pure titanium. Native oxide is removed from the Ti 6A1/4V alloy, followed by contacting the metal at ambient temperature with an aqueous hydrochloric acid solution containing a relatively small amount of hydrofluoric acid.
1. A method of producing a uniformly roughened surface on Ti 6/4 alloy for contact with living bone comprising:
(a) removing native oxide from said Ti 6/4 alloy to expose metal; and
(b) contacting said exposed metal with an aqueous solution of hydrofluoric acid and hydrochloric acid for a suitable period of time to create a desired surface topography having irregularities with peak-to-valley heights of less than 10 microns.
2. A method of claim 1 , wherein the roughened surface has peak distances of about 1-3 μm.
3. A method of claim 1 , wherein said native oxide is removed by contacting said Ti 6/4 alloy with a second aqueous solution of hydrofluoric acid for a suitable period of time.
4. A method of claim 3 wherein said second aqueous solution contains about 7.9 to 9.0 wt % hydrofluoric acid.
5. A method of claim 4 wherein said aqueous solution contains about 0.005 to 1.0 wt % hydrofluoric acid and about 10 to 30 wt % hydrochloric acid.
6. A method of claim 5 wherein said aqueous solution contains about 0.0845 wt % hydrofluoric acid and about 20 wt % hydrochloric acid.
7. A method of producing a uniformly roughened surface on Ti 6/4 alloy for contact with living bone comprising:
(a) removing native oxide from said Ti 6/4 alloy to expose metal by contacting said alloy with an aqueous solution of hydrofluoric acid for a suitable period of time;
(b) rinsing said alloy after said native oxide removal of (a);
(c) contacting said exposed metal in an aqueous solution of about 0.005 to 1.0 wt % hydrofluoric acid and about 10 to 30 wt % hydrochloric acid at room temperature for a suitable period of time to create a desired surface topography having irregularities with peak-to-valley heights of less than 10 microns; and
(d) rinsing the surface produced in step (c) to remove the residual aqueous solution of (c).
8. A method of claim 7 wherein said aqueous solution of step (a) contains about 7.9 to 9.0 wt % hydrofluoric acid.
9. A method of claim 8 wherein said aqueous solution of step (a) contains about 8.45 wt % hydrofluoric acid.
10. A method of claim 7 wherein said aqueous solution of step (c) contains about 0.053 to 0.105 wt % hydrofluoric acid and about 19 to 21 wt % hydrochloric acid.
11. A method of claim 10 wherein said aqueous solution of step (c) contains about 0.0845 wt % hydrofluoric acid and about 20 wt % hydrochloric acid.
12. A dental implant of Ti 6/4 alloy for contact with living bone comprising:
(a) a head section for mounting dental prosthesis components;
(b) a threaded section for engaging said living bone; and
(c) a neck section disposed between said head section and said threaded section;
wherein at least a portion of said threaded section has a desired roughened surface topography having irregularities with peak-to-valley heights of less than 10 microns created by etching said threaded portion with an aqueous solution of about 0.005 to 1.0 wt % hydrofluoric acid and about 10 to 30 wt % hydrochloric acid.
13. A dental implant of claim 12 wherein native oxide is removed from said threaded portion prior to said etching with an aqueous solution of hydrofluoric acid and hydrochloric acid.
14. A dental implant of claim 13 wherein said native oxide is removed by contacting said threaded portion with a second aqueous solution of hydrofluoric acid.
15. A dental implant of claim 14 wherein said second aqueous solution contains about 7.9 to 9.0 wt % hydrofluoric acid.
16. A dental implant of claim 12 wherein said aqueous solution contains about 0.0845 wt % hydrofluoric acid and about 20 wt % hydrochloric acid.
17. A method of producing a uniformly roughened surface of Ti 6/4 alloy for contact with living bone comprising:
(a) removing native oxide from said Ti 6/4 alloy to produce an exposed metal surface; and
(b) etching said exposed metal surface with Keller's Solution to create a desired surface topography having irregularities with peak-to-valley heights of less than 10 microns.
18. A dental implant assembly comprising:
a threaded section comprising Ti 6/4 alloy adapted to engage living bone; and
a head section located above the threaded section,
wherein at least a portion of the threaded section has a roughened surface topography having irregularities with peak-to-valley heights of less than 10 microns created by etching with an aqueous solution comprising hydrofluoric acid and hydrochloric acid.
19. The dental implant assembly of claim 18 , further comprising a neck section positioned between the head section and the threaded section, the head section being adapted to engage dental prosthesis components, wherein the threaded section directly below the neck section has a roughened surface topography having irregularities with peak-to-valley heights of less than 10 microns.
20. A method of producing a uniformly roughened surface on a dental implant for contact with living bone, the dental implant being made of Ti 6/4 alloy and having a head section, a neck section below the head section, and a threaded section below the neck section, the method comprising:
(a) removing native oxide from the neck section and the threaded section to create an exposed metal surface; and
(b) contacting the exposed metal surface including the neck section and the threaded section directly below the neck section with an aqueous solution of hydrofluoric acid and hydrochloric acid for a suitable period of time to create a desired surface topography having irregularities with peak-to-valley heights of less than 10 microns.