Al-Cu-Li-Mg-Ag-Mn-Zr alloy for use as structural members requiring high strength and high fracture toughness
View Patent ↗An improved aluminum lithium alloy comprising 0.1 to 2.5 wt. % Li, 2.5 to 5.5 wt. % Cu, 0.2 to 1.0 wt. % Mg, 0.2 to 0.8 wt. % Ag, 0.2 to 0.8 wt. % Mn, up to 0.4 wt. % Zr or other grain refiner such as chromium, titanium, hafnium, scandium or vanadium, the balance aluminum. The present alloy exhibits an improved combination of strength and fracture toughness, over any thickness range. The present invention is further directed to methods for preparing and using Al—Li alloys as well as to products comprising the same.
1. An aluminum alloy having improved strength and fracture toughness, said alloy comprising the following alloying elements added thereto:
Cu: 2.5-4.0 wt.%
Li: 0.8-2.5 wt.%
Mg: 0.2-1 wt.%
Ag: 0.2-0.8 wt.%
Mn: 0.2-0.8 wt.% and
Zr: 0.05 -0.3 wt. %;
And wherein the balance is Al and normal and/or inevitable elements and impurities.
2. An alloy according to claim 1 , comprising 3 to 4 wt. % copper.
3. An alloy according to claim 1 , comprising 0.8 to 1.8 wt. % lithium.
4. An alloy according to claim 3 , comprising 0.8 to 1.2 wt. % lithium.
5. An alloy according to claim 1 , comprising 0.8 to 1.5 wt. % lithium.
6. An alloy according to claim 1 , comprising 0.3 to 0.5 wt. % magnesium.
7. An alloy according to claim 1 , comprising 0.3 to 0.5 wt. % silver.
8. An alloy according to claim 1 , comprising 0.05 to 0.15% zirconium.
9. A rolled product comprising an aluminum alloy according to claim 8 , with a thickness of less than about 3 inches (76.2 mm), exhibiting in a solution heat-treated, quenched, stress-relieved and artificially aged condition at least one set of properties selected from the group consisting of:
(a) UTS (L)>76 ksi (524.0 MPa) and K IC (L)>35 ksi√inch (38.5 MPa√m),
(b) TYS (L)>71 ksi (489.5 MPa) and K IC (L)>35 ksi√inch (38.5 MPa√m),
(c) UTS (LT)>75 ksi 517.1 MPa) and K IC (L-T)>29 ksi√inch (31.9 MPa√m),
(d) TYS (LT)>68 ksi (468.8 MPa) and K IC (L-T)>29 ksi√inch (31.9 MPa√m),
(e) UTS (ST)>76 ksi (524.0 MPa) and K IC (S-T)>26 ksi√inch (28.6 MPa√m) and
(f) TYS (ST)>65 ksi (448.2 MPa) and K IC (S-T)>26 ksi√inch (28.6 MPa√m).
10. A rolled product comprising an aluminum alloy according to claim 1 , with a thickness of at least about 3 inches, exhibiting in a solution heat-treated, quenched, stress-relieved and artificially aged condition, at least one set of properties selected from the group consisting of:
(a) UTS (L)>70 ksi (482.6 MPa) and K IC (L)>34 ksi√inch (37.4 MPa√m),
(b) TYS (L)>65 ksi (448.2 MPa) and K IC (L)>34 ksi√inch (37.4 MPa√m),
(c) UTS (LT)>70 ksi (482.6 MPa) and K IC (L-T)>27 ksi√inch (29.7 MPa√m),
(d) TYS (LT)>62 ksi (427.5 MPa) and K IC (L-T)>26 ksi√inch (28.6 MPa√m),
(e) UTS (ST)>70 ksi (482.6 MPa) and K IC (S-T)>24 ksi√inch (26.4 MPa√m) and
(f) TYS (ST)>60 ksi (413.7 MPa) and K IC (S-T)>23 ksi√inch (25.3 MPa√m).
11. A structural product comprising an alloy of claim 1 .
12. A structural product of claim 11 comprising a rolled product.
13. A structural product of claim 11 comprising a sheet, plate forging, extrusion, spar and/or welded assembly.
14. An alloy of claim 1 , that has been subjected to at least one of (i) homogenization, (ii) hot rolling, (iii) solution heat treatment, (iv) water quench, (v) stretching, and/or (vi) aging.
15. An aluminum alloy of claim 1 comprising from 0.3-0.8 Mn.
16. A structural product comprising an alloy of claim 15 .