Molded thin-layer lignocellulosic composites made using hybrid poplar and methods of making same
View Patent ↗Thin-layer lignocellulosic composites made using hybrid poplar and methods for the manufacture of such thin-layer composites are disclosed. Also described is a process for making thin-layer lignocellulosic composite door skins using hybrid poplar wood fiber.
1. A method for making a thin-layer lignocellulosic composite comprising a predetermined amount of hybrid poplar (hybrid Populus ) comprising the steps of:
(a) forming a mixture comprising a refined lignocellulose fiber comprising a predetermined amount of hybrid poplar fiber, a resin, a release agent that will not interfere with subsequent processing of the thin-layer lignocellulosic composite, and at least one type of wax;
(b) pre-pressing the mixture into a loose mat; and
(c) pressing the mat between two dies at an elevated temperature and pressure and for sufficient time to form a thin-layer lignocellulosic composite, wherein at least one of the two dies is coated with an anti-bonding agent comprising at least one silicone and/or silane based chemical.
2. The method of claim 1 , wherein the hybrid poplar comprises the total lignocellulose fiber used in the thin-layer composite.
3. The method of claim 1 , wherein the hybrid poplar fiber ranges from about 40% to about 75% of the total lignocellulose fiber used in the thin-layer composite.
4. The method of claim 1 , wherein the hybrid poplar fiber ranges from about 40% to about 55% of the total lignocellulose fiber used in the thin-layer composite.
5. The method of claim 1 , wherein the total lignocellulose fiber ranges from about 80% to about 95% by weight of the thin-layer composite.
6. The method of claim 1 , wherein the step of forming a mixture comprising a refined lignocellulose fiber-comprising a predetermined amount of hybrid poplar fiber, a resin, a release agent and at least one type of wax comprises spraying at least one surface of the mat with a release agent prior to pressing the mat.
7. The method of claim 1 , further comprising adding a pre-press sealer to at least one surface of the mat prior to pressing the mat.
8. The method of claim 1 , wherein the final density of the thin-layer lignocellulosic composite ranges from about 45 pounds per cubic foot to about 58 pounds per cubic foot.
9. The method of claim 1 , wherein the final density of the thin-layer lignocellulosic composite ranges from about 51 pounds per cubic foot to about 56 pounds per cubic foot.
10. The method of claim 1 , wherein the thickness of the thin-layer lignocellulosic composite ranges from about 0.05 inches to about 0.5 inches.
11. The method of claim 1 , wherein the thickness of the thin-layer lignocellulosic composite ranges from about 0.08 inches to about 0.2 inches.
12. The method of claim 1 , wherein the thickness of the thin-layer lignocellulosic composite ranges from about 0.09 inches to about 0.115 inches.
13. The method of claim 1 , wherein the thin-layer lignocellulosic composite comprises a door skin.
14. The method of claim 13 , wherein the lignocellulose used to generate the refined fibers comprises less than 20% fines, wherein fines comprise particles able to pass through a 1/16 inch by 1/16 inch (1.59 mm by 1.59 mm) mesh.
15. The method of claim 13 , wherein the use of hybrid poplar fiber results in a reduction in the workload for the refiner used to refine the fiber in the range of 5% to 20% as compared to a door skin having less than 1% hybrid poplar wood.
16. The method of claim 13 , wherein the use of hybrid poplar fiber results in a reduction in the amount of resin per door skin in the range of about 5% to 20% as compared to a door skin having less than 1% hybrid poplar wood.
17. The method of claim 13 , wherein the use of hybrid poplar fiber results in a reduction in the weight per door skin in the range of about 5% to 20% as compared to a door skin having less than 1% hybrid poplar wood.
18. A method for making a thin-layer lignocellulosic composite comprising a predetermined amount of hybrid poplar (hybrid Populus ) comprising the steps of:
(a) forming a mixture comprising a refined lignocellulose fiber comprising a predetermined amount of hybrid poplar fiber, a resin, at least one type of wax, and, optionally, a release agent that is distinct from the wax and that will not interfere with subsequent processing of the thin-layer lignocellulosic composite;
(b) pre-pressing the mixture into a loose mat; and
(c) pressing the mat between two dies at an elevated temperature and pressure and for sufficient time to form a thin-layer lignocellulosic composite, wherein at least one of the two dies is coated with an anti-bonding agent comprising at least one silane and/or silicone based chemical.