Ductile medium-and high-density, non-toxic shot and other articles and method for producing the same
View Patent ↗Density-enhanced compositions that are comprised of at least iron and tungsten, and articles, including firearm projectiles, formed therefrom. The articles have a density that exceeds that of steel, and which may be less than, equal to, or greater than that of lead. In some embodiments, iron is the majority component and tungsten is a minority component, with steel optionally forming a portion of the iron-containing component. In some embodiments, the article includes at least one additional minority component, such as one or more of nickel, manganese, tin, carbon, steel, chromium, molybdenum, silicon, aluminum, zinc, copper, potassium, sulfur, vanadium, and/or titanium. In some embodiments, the article is cast or otherwise formed from molten material, and in some embodiments the article is formed via powder metallurgy. In some embodiments, the article is firearm shot, a firearm slug, or a bullet.
1. A shotgun shell, comprising:
a casing containing at least wadding, a charge and a primer;
a plurality of shell shot within the casing, wherein the shell shot are at least substantially formed from a cast alloy comprising:
20-35 wt % tungsten;
5-20 wt % nickel; and
50-75 wt % iron.
2. The shell of claim 1 , wherein the cast alloy further comprises steel.
3. The shell of claim 1 , wherein the cast alloy further comprises manganese.
4. The shell of claim 1 , wherein the cast alloy contains ferrotungsten.
5. The shell of claim 1 , wherein the cast alloy has a density in the range of 8-10.5 g/cc.
6. The shell of claim 1 , wherein the cast alloy has a density in the range of 10.5-15 g/cc.
7. The shell of claim 1 , wherein the alloy includes 10-20 wt % nickel.
8. The shell of claim 1 , wherein the alloy has a hardness of less than 275 Brinell.
9. The shell of claim 1 , wherein the alloy has a hardness of less than 270 Brinell.
10. The shell of claim 1 , wherein the alloy includes 20-30 wt % tungsten.
11. A shotgun shell, comprising:
casing containing at least wadding, a charge and a primer;
a plurality of shell shot within the casing, wherein the shell shot are at least substantially formed from a cast alloy comprising:
5-29.3 wt % tungsten;
5-20 wt % nickel; and
50-75 wt % iron.
12. The shell of claim 11 , wherein the cast alloy further comprises steel.
13. The shell of claim 11 , wherein the cast alloy further comprises manganese.
14. The shell of claim 11 , wherein the cast alloy contains ferrotungsten.
15. The shell of claim 11 , wherein the cast alloy has a density in the range of 8-10.5 g/cc.
16. The shell of claim 11 , wherein the cast alloy has a density in the range of 10.5-15 g/cc.
17. The shell of claim 11 , wherein the alloy includes 10-20 wt % nickel.
18. The shell of claim 11 , wherein the alloy has a hardness of less than 275 Brinell.
19. The shell of claim 11 , wherein the alloy has a hardness of less than 270 Brinell.
20. The shell of claim 11 , wherein the alloy includes 20-29.3 wt % tungsten.