Lithium-ion rechargeable battery with negative electrode material mixture comprising graphite and carbon nano-tubes
View Patent ↗A lithium-ion rechargeable battery, comprising a positive electrode capable of absorbing and desorbing lithium ions, a negative electrode capable of absorbing and desorbing lithium ions, a separator interposed between the positive electrode and the negative electrode, and a non-aqueous electrolyte, wherein the negative electrode comprises a negative electrode current collector and a negative electrode material mixture layer carried on the negative electrode current collector, the negative electrode material mixture layer comprises graphite and carbon nano-tubes, and an amount of the carbon nano-tubes in the negative electrode material mixture layer is not smaller than 0.1 part by weight and not larger than 10 parts by weight, per 100 parts by weight of the graphite.
1. A lithium-ion rechargeable battery, comprising:
a positive electrode capable of absorbing and desorbing lithium ions;
a negative electrode capable of absorbing and desorbing lithium ions;
a separator interposed between said positive electrode and said negative electrode; and
a non-aqueous electrolyte, wherein
said negative electrode comprises a negative electrode current collector and a negative electrode material mixture layer carried on said negative electrode current collector,
said negative electrode material mixture layer comprises graphite and carbon nano-tubes, said graphite being adhered with carbonized pitch, and
an amount of said carbon nano-tubes in said negative electrode material mixture layer is not smaller than 1 part by weight and not larger than 10 parts by weight, per 100 parts by weight of said graphite, wherein said carbon nano-tubes have an average fiber diameter of 50 μm or smaller, and an average fiber length of 5 μm or smaller.
2. The lithium-ion rechargeable battery in accordance with claim 1 , wherein said negative electrode material mixture layer has a density of not smaller than 1.4 g/cm 3 and not larger than 1.8 g/cm 3 .
3. A lithium-ion rechargeable battery in accordance with claim 1 , wherein said carbon nano-tubes have a multi-wall structure, an average fiber diameter of said carbon nano-tubes is 10 nm or larger, and an average fiber length of said carbon nano-tubes is 1 μm or larger.
4. The lithium-ion rechargeable battery in accordance with claim 1 , wherein said graphite has the following physical properties:
(1) a spacing d 002 between (002) crystal faces, obtained by a powder X-ray diffraction measurement, is 3.365 Å or less;
(2) an average particle size, obtained by a laser diffraction-type particle size distribution measurement, is not smaller than 5 μm and not larger than 25 μm;
(3) a BET specific surface area is 5 m 2 /g or smaller; and
(4) an average particle circularity is 0.85 or larger.