Carbo-nitrided case hardened martensitic stainless steels
View Patent ↗A carbo-nitriding process for forming a martensitic stainless steel, which is case hardened and superior corrosion resistance over carburized process, is provided. A process for forming a martensitic stainless steel which is case hardened is provided. The process comprises the steps of providing a material consisting essentially of from 8.0 to 18 wt % chromium, cobalt up to 16 wt %, vanadium up to 5.0 wt %, molybdenum up to 8.0 wt %, nickel up to 8.0 wt %, manganese up to 4.0 wt %, silicon up to 2.0 wt %, tungsten up to 6.0 wt %, titanium up to 2.0 wt %, niobium up to 4.0 wt % and the balance iron, and carbo-nitriding to prescribed levels of C+N, to form a hard, corrosion resistance case in a fracture tough stainless steel.
1. A process for forming a martensitic stainless steel which is case hardened comprising the steps of:
forming an article from a material consisting essentially of from 8.0 to 18 wt % chromium, cobalt up to 16 wt %, vanadium up to 0.5 wt %, molybdenum up to 8.0 wt %, nickel up to 8.0 wt %, manganese up to 4.0 wt %, silicon up to 2.0 wt %, tungsten up to 6.0 wt %, titanium up to 2.0 wt %, niobium up to 4.0 wt % and the balance iron; and
producing a hardened case containing from 0.2 to 0.55 wt % carbon and from 0.2 to 1.2 wt % nitrogen on said article;
said hardened case producing step comprising carbo-nitriding said article to form at least one of a hard martensite phase and nitride precipitates,
wherein said carbo-nitriding step comprises forming said at least one of a hard martensite phase and nitride precipitates by heating said material in an atmosphere containing carbon and nitrogen at a temperature in the range of 1650 degrees Fahrenheit to 2000 degrees Fahrenheit for a time in the range of from 40 to 200 hours.
2. A process according to claim 1 , wherein said carbo-nitriding step produces a hardened case having a total amount of carbon and nitrogen in the range of 0.5 to 1.7 wt %.
3. A process according to claim 1 , wherein said carbo-nitriding step comprises controlling carbon and nitrogen levels so that a chromium content of said carbo-nitrided case is greater than 8.0 wt %.
4. A process according to claim 1 , wherein said material providing step comprises providing a material consisting of 13 wt % chromium, 5.4 wt % cobalt, 1.8 wt % molybdenum, 2.6 wt % nickel, 0.6 wt % manganese, 0.6 wt % vanadium, 0.4 wt % silicon, 0.07 wt % carbon, and the balance iron.
5. A process according to claim 1 , wherein said material providing step comprises providing a material consisting of 14 wt % chromium, 12.4 wt % cobalt, 4.7 wt % molybdenum, 2.05 wt % nickel, 0.6 wt % vanadium, 0.05 wt % carbon, and the balance iron.
6. A process according to claim 1 , wherein said material providing step comprises providing a material consisting of 13.75 wt % chromium, 5.0 wt % cobalt, 3.0 wt % molybdenum, 3.0 wt % nickel, 0.08 wt % vanadium, 0.75 wt % manganese, 0.4 wt % silicon, 0.15 wt % carbon, and the balance iron.
7. A process according to claim 1 , wherein said material providing step comprises providing a material consisting of 14 wt % chromium, 5.0 wt % cobalt, 4.0 wt % molybdenum, 3.5 wt % nickel, 0.08 wt % vanadium, 0.22 wt % manganese, 0.3 wt % silicon, 0.15 wt % carbon, and the balance iron.
8. A process according to claim 1 , wherein said material providing step comprises providing a material consisting of 13.5 wt % chromium, 3.75 wt % cobalt, 3.5 wt % molybdenum, 3.0 wt % nickel, 0.08 wt % vanadium, 0.25 wt % manganese, 0.3 wt % silicon, 0.15 wt % carbon, and the balance iron.
9. A process according to claim 1 , wherein said material providing step comprises providing a material consisting of 13.5 wt % chromium, 3.75 wt % cobalt, 3.5 wt % molybdenum, 3.0 wt % nickel, 1.0 wt % titanium, 1.0 wt % manganese, 0.3 wt % silicon, 0.15 wt % carbon, and the balance iron.
10. A process according to claim 1 , wherein said material providing step comprises providing a material consisting of 15.25 wt % chromium, 5.0 wt % cobalt, 3.5 wt % molybdenum, 4.0 wt % nickel, 0.25 wt % vanadium, 0.2 wt % manganese, 0.25 wt % silicon, 0.15 wt % carbon, and the balance iron.
11. A process according to claim 1 , wherein said material providing step comprises providing a material consisting of 14 wt % chromium, 2.75 wt % cobalt, 3.25 wt % molybdenum, 3.5 wt % nickel, 0.3 wt % vanadium, 0.3 wt % manganese, 0.3 wt % silicon, 0.15 wt % carbon, and the balance iron.