Method of forming sputtering articles by multidirectional deformation
View Patent ↗A method of producing a valve metal mill form having dimensions sufficient to be divided to form a plurality of sputter targets is described. The method includes multidirectional deformation of an ingot to form a mill form having a preferred average grain size of about 100 microns or less and/or a texture substantially void of textural bands.
1. A method of producing a multidirectionally deformed valve metal having dimensions sufficient to be divided to form a plurality of sputter targets, comprising:
a first deforming of an ingot to form a preform slab having a first dimension, a second dimension normal to said first dimension, and a third dimension normal to said second dimension that is less than both said first and said second dimensions; and
a second deforming of said preform slab by increasing said third dimension and decreasing said second dimension such that said second dimension is made to be less than said third dimension to form an intermediate slab, wherein said intermediate slab has an average grain size of less than about 250 microns.
2. The method of claim 1 , further comprising partitioning said intermediate slab to form a plurality of rolling slabs.
3. The method of claim 1 , wherein said intermediate slab has a texture that is substantially void of textural bands.
4. The method of claim 1 , further comprising annealing said preform slab.
5. The method of claim 1 , further comprising annealing said intermediate slab.
6. The method of claim 1 , wherein said ingot is tantalum or niobium.
7. The method of claim 1 , wherein said ingot is formed by electron beam melting and casting.
8. The method of claim 1 , wherein said first deforming comprises forging, rolling, or any combination thereof.
9. The method of claim 1 , wherein said second deforming comprises forging, rolling, bloom rolling, or any combination thereof.
10. The method of claim 1 , wherein said second deforming comprises decreasing said second dimension by about 25 to about 80%.
11. The rolling slab formed by the method of claim 2 , wherein said rolling slab has an average grain size of about 100 microns or less.
12. The rolling slab formed by the method of claim 2 , wherein said rolling slab has an average grain size of about 50 microns or less.
13. A method of producing a multidirectionally deformed valve metal having dimensions sufficient to be divided to form a plurality of sputter targets, comprising:
a first deforming of an ingot to form a preform slab having a first dimension, a second dimension normal to said first dimension, and a third dimension normal to said second dimension that is less than both said first dimension and said second dimension;
a second deforming of said preform slab to form a rod, wherein said rod has an average grain size of less than about 250 microns; and
partitioning said rod to form a plurality of billets.
14. The method of claim 13 , wherein said rod has a texture that is substantially void of textural bands.
15. The method of claim 13 , further comprising annealing said preform slab.
16. The method of claim 13 , further comprising annealing said rod.
17. The method of claim 13 , wherein said ingot is tantalum or niobium.
18. The method of claim 13 , wherein said ingot is formed by electron beam melting and casting.
19. The method of claim 13 , wherein said first deforming and said second deforming comprises forging, rolling, or any combination thereof.
20. The billets formed by the method of claim 13 , wherein said billets have an average grain size of about 100 microns or less.
21. The billets formed by the method of claim 13 , wherein said billets have an average grain size of about 50 microns or less.
22. A method of producing a multidirectionally deformed valve metal having dimensions sufficient to be divided to form a plurality of sputter targets, comprising:
a first deforming of an ingot to form a preform slab having a first dimension, a second dimension normal to said first dimension, and a third dimension normal to said second dimension that is less than both said first dimension and said second dimension;
partitioning said preform slab transversely to said first dimension to form a plurality of intermediate slabs, wherein each intermediate slab has a first dimension that is less than said first dimension of said preform slab, a second dimension normal to said first dimension of said intermediate slab, and a third dimension normal to said second dimension of said intermediate slab that is less than both said first dimension and said second dimension of said preform slab; and
a second deforming of at least one of said intermediate slabs by increasing said third dimension of said at least one intermediate slab and decreasing said first dimension of said at least one intermediate slab such that said first dimension of said at least one intermediate slab is made to be less than said third dimension of said at least one intermediate slab to form a rolling slab, wherein said rolling slab has an average grain size of less than about 250 microns.
23. The method of claim 22 , wherein said rolling slab has a texture that is substantially void of textural bands.
24. The method of claim 22 , further comprising annealing said preform slab.
25. The method of claim 22 , further comprising annealing said at least of said intermediate slabs.
26. The method of claim 22 , wherein said ingot is tantalum or niobium.
27. The method of claim 22 , wherein said ingot is formed by electron beam melting and casting.
28. The method of claim 22 , wherein said first deforming and said second deforming comprises forging, rolling, or any combination thereof.
29. The method of claim 22 , wherein said second deforming comprises decreasing said first dimension of said intermediate slab by about 25 to about 80%.
30. The rolling slab formed by the method of claim 22 , wherein said rolling slab has an average grain size of from about 100 microns or less.
31. The rolling slab formed by the method of claim 22 , wherein said rolling slab has an average grain size of about 50 microns or less.
32. The method of claim 1 , wherein said intermediate slab has a uniform texture throughout the thickness.
33. The method of claim 1 , wherein said intermediate slab has a primary (111), a primary (100), or a mixed (111)(100) texture on the surface and/or throughout the thickness.
34. The method of claim 13 , wherein said rod has a uniform texture throughout the thickness.
35. The method of claim 13 , wherein said rod has a primary (111), a primary (100), or a mixed (111)(100) texture on the surface and/or throughout the thickness.
36. The method of claim 22 , wherein said rolling slab has a uniform texture throughout the thickness.
37. The method of claim 22 , wherein said rolling slab has a primary (111), a primary (100), or a mixed (111)(100) texture on the surface and/or throughout the thickness.