Pigment selection for photographic base stock
A coated paper, particularly useful as a photobase paper, includes a pigment coating on at least one side thereof wherein the pigment coating comprises aragonite precipitated calcium carbonate, hollow sphere pigment and, optionally high-aspect-ratio clay, with aspect ratio in the range of about 50 to about 100 and mixtures thereof. Methods for manufacturing the coated paper having a roughness of no more than 3 microns are also described.
1 . A method for producing a coated paper for use in forming a recording material comprising the steps of:
providing a base stock and
coating the base stock on at least one side thereof with a pigment coating composition comprising aragonite precipitated calcium carbonate, hollow sphere pigment and a binder to produce a coated paper.
2 . The method of claim 1 wherein said coated paper further comprises high-aspect-ratio clay, with aspect ratio in the range of about 50 to about 100.
3 . The method of claim 1 wherein the pigment coating coat weight is from about 4 to about 15 lb/3300 ft 2 .
4 . The method of claim 1 wherein the pigment coating comprises from about 40 to about 80% aragonite precipitated calcium carbonate and from about 15 to about 25% hollow sphere pigment by dry weight based on total pigment coating.
5 . The method of claim 4 wherein the pigment coating further comprises from about 20 to about 30% of an acrylic binder based on total pigment coating.
6 . The method of claim 5 wherein the binder comprises a styrene-acrylic binder.
7 . The method of claim 1 wherein the pigment coating is substantially free of clay.
8 . The method of claim 1 wherein the binder is present in the pigment coating composition at from about 8 to about 30% by weight of the dry pigment coating.
9 . The method of claim 8 wherein the pigment to binder ratio is within the range from about 100:15 to about 100:40.
10 . The method of claim 8 wherein the pigment coating comprises an acrylic binder selected from the group consisting of acrylic esters, modified acrylic esters, acrylic ester co-polymers, modified acrylic ester co-polymers and mixtures thereof.
11 . The method of claim 1 wherein the coated paper has a surface roughness of not more than about 2.0 micron Ra.
12 . The method of claim 1 wherein said hollow sphere pigment comprises a hollow sphere polystyrene pigment.
13 . The method of claim 1 further comprising:
subjecting the coated base stock to a smoothing operation to provide a coated paper having a roughness of not more than about 2.0 micron Ra.
14 . The method of claim 13 wherein said smoothing operation comprises passing the coated base stock through a plurality of nips at a load of from about 1000 to about 1500 pli.
15 . The method of claim 13 wherein said pigment coating comprises from about 20 to about 30% binder, from about 15 to about 25% hollow sphere pigment and from about 40 to about 80% aragonite precipitated calcium carbonate based on total pigment coating.
16 . The method of claim 13 wherein said binder comprises an acrylic binder selected from the group consisting of acrylic esters, modified acrylic esters, acrylic ester co-polymers, modified acrylic ester co-polymers and mixtures thereof.
17 . A support material for an image forming system comprising a coated paper wherein the coated paper comprises:
a base paper having a pigment coating on at least one side thereof wherein the pigment coating comprises aragonite precipitated calcium carbonate and hollow sphere pigment; and
an image forming or image receptive coating layer on at least one side of the coated paper wherein the image forming or image receptive coating is selected from the group consisting of a photosensitive emulsion, an ink jet receptive coating, a thermal dye recording layer and a pigment based ink receptive layer.
18 . The support material in accordance with claim 17 wherein the support material further comprises a polymeric coating layer disposed between the pigment coating on the coated paper and the image forming or image receptive coating layer on one or both sides of the support material.
19 . The support material in accordance with claim 18 wherein the polymeric coating layer comprises a polyolefin or polyester coating layer.
20 . The support material in accordance with claim 18 wherein the pigment coating coat weight is from about 4 to about 15 lb/3300 ft 2 .
21 . The support material in accordance with claim 20 wherein the pigment coating comprises from about 40 to about 80% aragonite precipitated calcium carbonate and from about 15 to 25% hollow sphere pigment by dry weight based on total pigment coating.
22 . The support material in accordance with claim 21 wherein the pigment coating further comprises from about 20 to about 30% of an acrylic binder based on total pigment coating.
23 . The support material in accordance with claim 22 wherein the pigment coating comprises from about 10 to about 14% high aspect ratio clay, from about 18 to about 22% hollow sphere polystyrene pigment and from about 65 to about 75% aragonite precipitated calcium carbonate based on total pigment weight.
24 . The support material in accordance with claim 21 wherein the pigment coating is substantially free of clay.
25 . The support material in accordance with claim 20 wherein the pigment coating further comprises a binder present in the pigment coating composition at from about 8 to about 30% by weight of the dry pigment coating.
26 . The support material in accordance with claim 25 wherein the pigment to binder ratio is within the range from about 100:15 to about 100:40.
27 . The support material in accordance with claim 25 wherein the pigment coating comprises an acrylic binder selected from the group consisting of acrylic esters, modified acrylic esters, acrylic ester co-polymers, modified acrylic ester co-polymers and mixtures thereof.
28 . The support material in accordance with claim 20 wherein the support material has a surface roughness of not more than about 2.0 micron Ra.
29 . The support material in accordance with claim 28 wherein the pigment coating comprises:
from about 10 to about 14% high aspect ratio clay, from about 18 to about 22% hollow sphere polystyrene pigment and from about 65 to about 75% aragonite precipitated calcium carbonate based on total pigment weight; and
from about 15 to about 25% of an acrylic binder by weight of the dry pigment coating.