Tire rubber composition comprising a coupling agent having a polythiosulfenamide function
View Patent ↗An elastomeric composition usable for the manufacture of tires, based on at least (i) a diene elastomer, (ii) an inorganic filler as reinforcing filler and (iii), as (inorganic filler/diene elastomer) coupling agent, a organosilicon compound which is at least bifunctional and can be grafted on to the elastomer by means of a sulfur group having a polythiosulfenamide function, of formula: ≡Si—A—S x —NR 1 R 2 , (I) in which: A is a divalent bond group, whether straight-chain or branched, which makes it possible to join the polythiosulfenamide group to a silicon atom of the organosilicon compound; x is an integer or fractional number of from 2 to 4; R 1 represents hydrogen or a monovalent hydrocarbon group; R 2 represents a monovalent hydrocarbon group selected from among C 3 -C 8 alkyls, whether straight-chain or branched, C 5 -C 10 cycloalkyls, C 6 -C 18 aryls and (C 6 -C 18 )aryl-(C 1 -C 8 )alkyls; R 1 and R 2 possibly forming together and with the nitrogen atom to which they are bonded a single hydrocarbon ring. Tires and tire treads comprising a composition of this type.
1. A tire comprising an elastomeric composition based on a diene elastomer, between 30 phr and 140 phr of silica as an inorganic filler and between 2 phr and 20 phr of a coupling agent comprising an organosilicon compound which is at least bifunctional and has a polythiosulfenamide function, and can be grafted on to the elastomer by means of a sulfur group, and which is selected from the group consisting of di(isopropyl)triethoxysilylpropyldithio-sulfenamide, di(isopropyl)ethoxydimethylsilylpropyldithio-sulfenamide, and mixtures of these compounds.
2. The tire according to claim 1 , wherein the diene elastomer is selected from the group consisting of polybutadienes, synthetic polyisoprenes, natural rubber, butadiene copolymers, isoprene copolymers and mixtures of these elastomers.
3. The tire according to claim 1 , wherein the inorganic filler is used in a mixture with carbon black.
4. The tire according to claim 3 , wherein the amount of carbon black is between 2 and 20 phr.
5. The tire according to claim 1 , wherein the coupling agent comprises di(isopropyl)ethoxydimethylsilylpropyldithio-sulfenamide of formula (III-3):