Ytterbium-barium silicate radiopaque glasses
View Patent ↗A family of radiopaque glasses comprising silicon dioxide (15–30%), ytterbium oxide (5–35%), barium oxide (30–50%) and fluoride (5–20%), all by weight. The family of glasses all exhibit high radiopacity with refractive indices varying from 1.508–1.592 and translucency ranging from clear to moderately opaque. These glasses can be incorporated into dental composites to provide radiopaque dental restoratives with a desired translucence and appearance.
1. A composite comprising:
(a) a resin; and
(b) a glass filler, said glass filler comprising the following ingredients:
(i) SiO 2 ;
(ii) Yb 2 O 3 ;
(iii) F;
(iv) BaO; and
(v) at least one component selected from the group consisting of Al 2 O 3 , P 2 O 5 , Al 2 O 3 —Na 2 O, Al 2 O 3 —K 2 O, Al 2 O 3 —P 2 O 5 , Al 2 O 3 —P 2 O 5 —Na 2 O and Al 2 O 3 —P 2 O 5 —K 2 .
2. The composite according to claim 1 wherein said composite is substantially radiopaque.
3. The composite according to claim 2 , wherein said composite is substantially clear.
4. The composite according to claim 2 , wherein said composite is substantially opaque.
5. A method of forming a substantially clear dental composite comprising, (a) providing a glass filler selected from the group consisting of SiO 2 —BaO—Yb 2 O 3 —F, SiO 2 — Al 2 O 3 — P 2 O 5 —Na 2 O—SrO— Yb 2 O 3 —F, SiO 2 — Al 2 O 3 —P 2 O 5 — Na 2 O —SrO— Yb 2 O 3 —F and SiO 2 —BaO— Yb 2 O 3 —F—R wherein R is selected from the group consisting of Al 2 O 3 , P 2 O 5 , Al 2 O 3 — Na 2 O, Al 2 O 3 — K 2 O, Al 2 O 3 — P 2 O 5 , B 2 O 3 — Na 2 O, Al 2 O 3 — P 2 O 5 — Na2O and Al 2 O 3 — P 2 O 5 — K 2 O; and (b) providing a resin with an index of refraction approximating that of said glass filler, such that the choice of said glass filler imparts the desired translucency to said dental composite and renders said dental composite substantially radiopaque.