Preliminary silica dispersion, fine silica dispersion, ink receiving layer coating solution and ink jet recording medium
View Patent ↗An ink jet recording medium including an ink receiving layer disposed on at least one side of a support, wherein the ink receiving layer is formed by applying an ink receiving layer coating solution. The ink receiving layer coating solution includes a water-soluble resin and a fine silica dispersion that has been prepared by finely dispersing a preliminary silica dispersion. The preliminary silica dispersion includes fumed silica, a cationic polymer having an I/O value of 2.4 or less, and alcohol.
1. A preliminary silica dispersion to be used in an ink receiving layer coating solution for forming an ink receiving layer of an ink jet recording medium, the preliminary silica dispersion comprising fumed silica, a cationic polymer having an I/O value of 2.4 or less, and alcohol.
2. The preliminary silica dispersion of claim 1 , which is produced by kneading the fumed silica with the cationic polymer having an I/O value of 2.4 or less and the alcohol.
3. The preliminary silica dispersion of claim 1 , wherein an average primary particle diameter of the fumed silica is 5 to 30 nm.
4. The preliminary silica dispersion of claim 1 , wherein the cationic polymer is contained in the preliminary silica dispersion in an amount of 1 to 15% by mass based on an amount of the fumed silica.
5. The preliminary silica dispersion of claim 1 , wherein the alcohol is contained in the preliminary silica dispersion in an amount of 0.1 to 20% by mass based on a solid content of the cationic polymer.
6. The preliminary silica dispersion of claim 1 , further comprising at least one of a nonionic surfactant and a cationic surfactant.
7. The preliminary silica dispersion of claim 1 , further comprising a water-miscible organic solvent.
8. A fine silica dispersion to be used in an ink receiving layer coating solution for forming an ink receiving layer of an ink jet recording medium, wherein the fine silica dispersion is prepared by further finely dispersing the preliminary silica dispersion of claim 1 .
9. The fine silica dispersion of claim 8 , wherein a surface of fine fumed silica particles is treated with a silane coupling agent.
10. An ink receiving layer coating solution for forming an ink receiving layer of an ink jet recording medium, comprising the fine silica dispersion of claim 8 and at least a water-soluble resin.
11. The ink receiving layer coating solution of claim 10 , wherein the water-soluble resin is polyvinyl alcohol-based resin.
12. The ink receiving layer coating solution of claim 11 , wherein the polyvinyl alcohol-based resin has a degree of saponification of 90% or more.
13. The ink receiving layer coating solution of claim 10 , wherein a ratio by mass of the fumed silica to the water-soluble resin is 1.5 to 10.
14. The ink receiving layer coating solution of claim 10 , further comprising a crosslinking agent.
15. The ink receiving layer coating solution of claim 14 , wherein the crosslinking agent is a boron compound.