View Patent ↗A niobium suboxide powder comprising 100 to 600 ppm of magnesium is described. The niobium suboxide powder may (alternatively or in addition to 100 to 600 ppm of magnesium) further include 50 to 400 ppm of molybdenum and/or tungsten. The niobium suboxide powder is suitable for the production of: capacitors having an insulator layer of niobium pentoxide; capacitor anodes produced from the niobium suboxide powder; and corresponding capacitors.
1. A niobium suboxide powder comprising 100 to 600 ppm of magnesium and a member selected from the group consisting of Fe, Cr, Ni, Cu, alkali metals, fluoride, chloride and combinations thereof.
2. A niobium suboxide powder comprising 50 to 400 ppm of a member selected from the group consisting of molybdenum, tungsten and combinations thereof.
3. A niobium suboxide powder comprising 100 to 600 ppm of magnesium, and 50 to 400 ppm of a member selected from the group consisting of molybdenum, tungsten and combinations thereof.
4. The niobium suboxide powder of claim 1 having a magnesium content of 150 to 400 ppm.
5. The niobium suboxide powder of claim 2 having a molybdenum content of 60 to 250 ppm.
6. The niobium suboxide powder of claim 1 , 2 , 3 , 4 or 5 which further comprises a member selected from the group consisting of Fe, Cr, Ni, Cu, alkali metals, fluoride, chloride and combinations thereof, wherein each member is independently present in an amount of less than 15 ppm.
7. The niobium suboxide powder according to claim 6 wherein said member selected from the group consisting of Fe, Cr, Ni, Cu, alkali metals, fluoride, chloride and combinations thereof, is present in an amount totalling less than 35 ppm.
8. The niobium suboxide powder of claim 3 having a carbon content of less than 40 ppm.
9. The niobium suboxide powder of claim 3 having a nitrogen content of 10 to 500 ppm.
10. The niobium suboxide powder of claim 1 wherein the mean composition of said niobium suboxide is represented by the formula, NbO x wherein 0.7<×<1.3.
11. The niobium suboxide powder of any of claims 1 to 3 comprising agglomerated primary particles having a diameter of from 0.3 to 1.5 μm.
12. A niobium suboxide anode comprising a sintered powder of the niobium suboxide powder of claim 1 .
13. A solid electrolyte capacitor comprising the niobium suboxide anode of claim 12 , and a barrier layer comprising niobium pentoxide.
14. The niobium suboxide powder of claim 1 having a carbon content of less than 40 ppm.
15. The niobium suboxide powder of claim 1 having a nitrogen content of 10 to 500 ppm.
16. The niobium suboxide powder of claim 3 wherein the mean composition of said niobium suboxide is represented by the formula, NbO x wherein 0.7<×<1.3.
17. A niobium suboxide anode comprising a sintered powder of the niobium suboxide powder of claim 3 .
18. A solid electrolyte capacitor comprising the niobium suboxide anode of claim 17 , and a barrier layer comprising niobium pentoxide.
19. The niobium suboxide powder of claim 2 having a magnesium content of 150 to 400 ppm.
20. The niobium suboxide powder of claim 3 having a magnesium content of 150 to 400 ppm.