Straight angle conductor and method of manufacturing the same
View Patent ↗A straight angle conductor 10 is provided with a cladding material including a core-sheet metal 11 and conductor-sheet metals 12 a, 12 b that sandwich both surfaces of the core-sheet metal 11 . The conductor-sheet metals 12 a, 12 b having a volume resistivity equal to or less than 5.0 (μΩ·cm) wraps both sides of the core-sheet metal 11 having a thermal expansion coefficient equal to or less than 10 (×10 −6 /C. °) to prevent the core-sheet metal 11 from being exposed to an outside of the conductor-sheet metals 12 a, 12 b . As a result, it prevents occurrence of an electrical potential difference in a boundary side face between the core-sheet metal 11 and the conductor-sheet metals 12 a, 12 b to improve corrosion resistance. Especially even when the straight angle conductor 10 is used on a silicon crystal wafer for a solar cell, damage of the silicon crystal wafer caused by heat occurring in soldering process of the conductor 10 or a change in temperature on use thereof for a solar cell is avoided.
1. A straight angle conductor for a lead wire, comprising:
a cladding material comprising a core-sheet metal and a conductor-sheet metal that sandwiches both surfaces of the core-sheet metal,
wherein the conductor-sheet metal wraps both side end faces of the core-sheet metal to prevent the core-sheet metal from being exposed to an outside of the conductor-sheet metal,
wherein the conductor-sheet metal has a crystal orientation with the following feature:
IR=I (111)/{ I (200)+ I (111)}≧0.15,
where I (111) represents X ray diffraction intensity of Surface (111), and I (200) represents X ray diffraction intensity of Surface (200), and
wherein the conductor-sheet metal is formed of Cu, Au, or Ag, or an alloy material comprising Cu or Au, and
wherein the core-sheet metal has a Vickers hardness equal to or less than 150 Hv and the conductor-sheet metal has a Vickers hardness equal to or less than 100 Hv.
2. The straight angle conductor as defined in claim 1 , wherein:
the core-sheet metal is formed of an alloy material of Fe—Ni.
3. The straight angle conductor as defined in claim 1 , further comprising:
a solder layer that coats an entirety or a part of an outer surface of the cladding material.
4. The straight angle conductor as defined in claim 3 , wherein:
the solder layer includes a Sn—Pb solder layer.
5. The straight angle conductor as defined in claim 3 , wherein:
the solder layer includes a Pb-free solder layer.
6. The straight angle conductor as defined in claim 5 , wherein:
the Pb-free solder layer is made of a Sn—Ag—Cu base alloy.
7. The straight angle conductor as defined in claim 6 , wherein: the Sn—Ag—Cu base alloy further includes at least one of In and P.
8. A straight angle conductor for a lead wire, comprising:
a cladding material comprising a core-sheet metal and a conductor-sheet metal that sandwiches both surfaces of the core-sheet metal,
wherein the conductor-sheet metal having a volume resistivity equal to or less than 5.0 μΩ·cm wraps both side end faces of the core-sheet metal having a thermal expansion coefficient equal to or less than 10×10 −6 /° C. to prevent the core-sheet metal from being exposed to an outside of the conductor-sheet metal,
wherein the conductor-sheet metal has a crystal orientation with the following feature:
IR=I (111)/{ I (200)+ I (111)}≧0.15.
where I (111) represents X ray diffraction intensity of Surface (111), and I (200) represents X ray diffraction intensity of Surface (200),
wherein the conductor-sheet metal is formed of Cu, Au, or Ag, or an alloy material comprising Cu or Au, and
wherein the core-sheet metal has a Vickers hardness equal to or less than 150 Hv and the conductor-sheet metal has a Vickers hardness equal to or less than 100 Hv.
9. A straight angle conductor for a lead wire, comprising:
a cladding material comprising a core-sheet metal having a thermal expansion coefficient equal to or less than 10×10 −6 /° C. and a conductor-sheet metal having a volume resistivity equal to or less than 5.0 μΩ·cm that sandwiches both surfaces of the core-sheet metal,
wherein the conductor-sheet metal has a crystal orientation with the following feature:
IR=I (111)/{ I (200)+ I (111)}≧0.15.
where I (111) represents X ray diffraction intensity of Surface (111), and I (200) represents X ray diffraction intensity of Surface (200),
wherein the conductor-sheet metal is formed of Cu, Au, or Ag, or an alloy material comprising Cu or Au, and
wherein the core-sheet metal has a Vickers hardness equal to or less than 150 Hv and the conductor-sheet metal has a Vickers hardness equal to or less than 100 Hv.