Method and composition for coating mat and articles produced therewith
View Patent ↗A coated glass mat comprises a glass mat substrate having non-woven glass fibers and a coating which essentially uniformly penetrates the glass mat substrate to desired fractional thickness of the coated glass mat. The coating imparts a tensile strength to the coated glass mat which on average is at least 1.33 times greater than the tensile strength of the glass mat substrate without the coating. In example embodiments, penetration of the coating into the glass mat substrate preferably extends to a depth of from twenty five percent of a thickness of the coated glass mat to seventy five percent of the thickness of the coated glass mat. Moreover, a non-coated thickness of the coated glass mat is sufficiently thick for bonding purposes with, e.g., a gypsum slurry or other core materials such as thermoplastic or thermosetting plastics. The coating has a porosity in a range of from 1.3 CFM to 5.0 CFM, e.g., the coating comprises a coating blend which provides the coated glass mat with a porosity sufficient to allow water vapor to escape from a gypsum slurry when heated. The coating is preferably a coating blend comprised of water, latex binder, inorganic pigment, and inorganic binder.
1. A method of forming a coated glass mat comprising:
conveying a glass mat substrate having non-woven glass fibers into contact with an applicator roll;
applying a coating comprising latex binder and inorganic pigment to the glass mat substrate having non-woven glass fibers with a surface of the applicator roll to form the coated glass mat;
said coating being only partially permeated into said substrate while also imparting a tensile strength to the coated glass mat which on average in a machine direction is at least 1.33 times greater than the tensile strength of the glass mat substrate without the coating,
said coated glass mat having a porosity in a range of from 1.3 CFM to 5.0 CFM per square foot.
2. The method of claim 1 , wherein the coating further comprises an inorganic binder.
3. The method of claim 1 , wherein said non-woven glass mat substrate before coating weighs between about twelve pounds per thousand square feet and about fifty pounds per thousand square feet.
4. The method of claim 1 , wherein the non-woven glass mat substrate before coating weighs about fourteen and a half (14.5) pounds per thousand square feet and wherein after coating the coated glass mat has a tensile strength which on average is greater than one hundred twenty pounds per three-inch width.
5. The method of claim 1 , wherein the glass mat substrate before coating weighs about twenty-six and a half (26.5) pounds per thousand square feet and wherein after coating the coated glass mat has a tensile strength which on average is greater than two hundred twenty pounds per three-inch width.
6. The method of claim 1 , wherein penetration of the coating into the glass mat substrate extends a depth of from twenty five percent of a thickness of the coated glass mat to seventy five percent of the thickness of the coated glass mat.
7. The method of claim 1 , wherein the coating uniformly penetrates the glass mat substrate to a desired fractional thickness of the coated glass mat.
8. The method of claim 1 , wherein, on average, the weight of the coated glass mat per unit area is no more than about six times the weight of the glass mat substrate prior to coating.
9. A method of forming a coated glass mat comprising:
conveying a glass mat substrate having non-woven glass fibers through a coating station;
in the coating station, forming the coated glass mat by applying a coating comprising latex binder and inorganic pigment to the glass mat substrate having non-woven glass fibers in such a manner that the coating is only partially permeated into said substrate while also imparting a tensile strength to the coated glass mat which on average in a machine direction is at least 1.33 times greater than the tensile strength of the glass mat substrate without the coating.
10. The method of claim 9 , further comprising applying the coating in such a manner that the coated glass mat has a porosity in a range of from 1.3 CFM to 5.0 CFM per square foot.
11. The method of claim 9 , wherein the coating further comprises an inorganic binder.
12. The method of claim 9 , wherein said non-woven glass mat substrate before coating weighs between about twelve pounds per thousand square feet and about fifty pounds per thousand square feet.
13. The method of claim 9 , wherein the non-woven glass mat substrate before coating weighs about fourteen and a half (14.5) pounds per thousand square feet and wherein after coating the coated glass mat has a tensile strength which on average is greater than one hundred twenty pounds per three-inch width.
14. The method of claim 9 , wherein the glass mat substrate before coating weighs about twenty-six and a half (26.5) pounds per thousand square feet and wherein after coating the coated glass mat has a tensile strength which on average is greater than two hundred twenty pounds per three-inch width.
15. The method of claim 9 , wherein penetration of the coating into the glass mat substrate extends a depth of from twenty five percent of a thickness of the coated glass mat to seventy five percent of the thickness of the coated glass mat.
16. The method of claim 9 , wherein the coating uniformly penetrates the glass mat substrate to a desired fractional thickness of the coated glass mat.
17. The method of claim 9 , wherein, on average, the weight of the coated glass mat per unit area is no more than about six times the weight of the glass mat substrate prior to coating.