2000 Series alloys with enhanced damage tolerance performance for aerospace applications
View Patent ↗The invention provides a 2000 series aluminum alloy having enhanced damage tolerance, the alloy consisting essentially of about 3.0-4.0 wt % copper; about 0.4-1.1 wt % magnesium; up to about 0.8 wt % silver; up to about 1.0 wt % Zn; up to about 0.25 wt % Zr; up to about 0.9 wt % Mn; up to about 0.5 wt % Fe; and up to about 0.5 wt % Si, the balance substantially aluminum, incidental impurities and elements, said copper and magnesium present in a ratio of about 3.6-5 parts copper to about 1 part magnesium. The alloy is suitable for use in wrought or cast products including those used in aerospace applications, particularly sheet or plate structural members, extrusions and forgings, and provides an improved combination of strength and damage tolerance.
1. A 2000 series aluminum-based alloy having enhanced damage tolerance consisting essentially of:
about 3.0 to about 4.0 wt % copper;
about 0.4 to about 1.1 wt % magnesium;
about 0.2 to about 0.8 wt % silver;
up to about 0.6 wt % Zn, wherein the zinc is partially substituted for the silver and a combined amount of zinc and silver is up to about 0.9 wt %;
up to about 0.25 wt % Zr;
up to about 0.9 wt % Mn;
a combined Si and Fe content of about 0.25 wt % or less;
the balance substantially aluminum, incidental impurities and elements, said copper and magnesium present in a ratio of about 3.6-4.5 parts copper to about 1 part magnesium.
2. The aluminum-based alloy of claim 1 , further comprising a grain refiner.
3. The aluminum-based alloy of claim 2 , wherein said grain refiner is titanium or a titanium compound, and said titanium or titanium compound is present in an amount ranging up to about 0.1 wt %.
4. The aluminum-based alloy of claim 1 , wherein said zirconium is present in an amount ranging up to about 0.18 wt %.
5. The aluminum-based alloy of claim 1 , wherein said manganese is present in an amount ranging from about 0.3-0.6 wt %.
6. The aluminum-based alloy of claim 1 , wherein the combined amount of said iron and said silicon is up to about 0.25 wt %.
7. The aluminum-based alloy of claim 1 , further comprising scandium.
8. The aluminum-based alloy of claim 7 , wherein said scandium is present in amount ranging up to about 0.25 wt %.
9. The aluminum-based alloy of claim 1 , further comprising an oxidation-controlling element.
10. The aluminum-based alloy of claim 9 , wherein said oxidation-controlling element is beryllium or calcium.
11. A wrought or cast product made from an aluminum-based alloy having enhanced damage tolerance consisting essentially of:
about 3.0 to about 4.0 wt % copper;
about 0.4 to about 1.1 wt % magnesium;
from about 0.2 to about 0.8 wt % silver;
up to about 0.6 wt % Zn, wherein the zinc is partially substituted for the silver and a combined amount of zinc and silver is up to about 0.9 wt %;
up to about 0.25 wt % Zr;
up to about 0.9 wt % Mn;
a combined Fe and Si content of up to about 0.25 wt % or less;
the balance substantially aluminum, incidental impurities and elements, said copper and magnesium present in a ratio of about 3.6-4.5 parts copper to about 1 part magnesium.
12. The wrought or cast product of claim 11 , further comprising a grain refiner.
13. The wrought or cast product of claim 12 , wherein said grain refiner is titanium or a titanium compound, and said titanium or titanium compound is present in an amount ranging up to about 0.1 wt %.
14. The wrought or cast product of claim 11 , wherein said zirconium is present in an amount ranging up to about 0.18 wt %.
15. The wrought or cast product of claim 11 , wherein said manganese is present in an amount ranging from about 0.3-0.6 wt %.
16. The wrought or cast product of claim 11 , wherein the combined amount of said iron and said silicon is up to about 0.25 wt %.
17. The wrought or cast product of claim 11 , further comprising scandium.
18. The wrought or cast product of claim 17 , wherein said scandium is present in amount ranging up to about 0.25 wt %.
19. The wrought or cast product of claim 11 , further comprising an oxidation-controlling element.
20. The wrought or cast product of claim 19 , wherein said oxidation-controlling element is beryllium or calcium.
21. The wrought or cast product of claim 11 , wherein said product is an aerospace, sheet, plate, forged or extruded product.
22. The aerospace product of claim 21 , wherein said product has a temper selected from the group consisting of T3, T39, T351, T6 and T8.
23. A metal matrix composite product made from an aluminum-based alloy having enhanced damage tolerance consisting essentially of:
about 3.0 to about 4.0 wt % copper;
about 0.4 to about 1.1 wt % magnesium;
from about 0.2 to about 0.8 wt % silver;
up to about 0.6 wt % Zn, wherein the zinc is partially substituted for the silver and a combined amount of zinc and silver is up to about 0.9 wt %;
up to about 0.25 wt % Zr;
up to about 0.9 wt % Mn;
a combined Fe and Si content of tip to about 0.25 wt % or less Si;
the balance substantially aluminum, incidental impurities and elements, said copper and magnesium present in a ratio of about 3.6-4.5 parts copper to about 1 part magnesium.