View Patent ↗This invention relates to a blend of fibers for use in protective clothing, a lightweight fabric made from such blend, protective articles made from the blend or fabric, and methods for making the fabric. The protective fabrics and articles of this invention have the unique combination of being comfortable, being highly effective against electrical arcs and flash fire hazards and having a pleasing appearance. Specifically, these fabrics can be processed to give the look and feel similar to conventional clothing fabrics such as denim fabrics.
1. A fiber blend for use in protective apparel, comprising:
(i) amorphous meta-aramid fiber,
(ii) crystallized meta-aramid fiber, and
(iii) flame retardant cellulosic fiber
wherein the meta-aramid fiber in the blend is in a range from 50 to 85 weight percent and wherein the total amount of meta-aramid fiber is in a range from one-third to two thirds amorphous and in a range from two thirds to one third crystalline by weight.
2. The fiber blend of claim 1 additionally comprising para-aramid fiber.
3. The fiber blend of claim 1 additionally comprising antistatic fiber.
4. The fiber blend of claim 1 wherein the crystallized meta-aramid fiber is pigmented, dyed, or colored.
5. A fabric comprising the fiber blend of claim 1 .
6. A protective article comprising the fiber blend of claim 1 .
7. The fiber blend of claim 1 wherein the meta-aramid fiber is present in a range from 60 to 75 weight percent.
8. A fabric for use in protective apparel, comprising:
(i) a first yarn comprising amorphous meta-aramid fiber and flame retardant cellulosic fiber, and
(ii) a second yarn comprising crystallized meta-aramid fiber and flame retardant cellulosic fiber
wherein the meta-aramid fiber in the fabric is in a range from 50 to 85 weight percent and wherein the total amount of meta-aramid fiber is in a range from one-third to two thirds amorphous and in a range from two thirds to one third crystalline by weight.
9. The fabric of claim 8 also containing para-aramid fiber.
10. The fabric of claim 8 also containing antistatic fiber.
11. The fabric of claim 8 wherein the yarns comprising crystallized meta-aramid fiber are pigmented, dyed, or colored.
12. The fabric of claim 8 wherein the yarns comprising amorphous meta-aramid fiber are dyed.
13. The fabric of claim 8 wherein the yarns comprising amorphous meta-aramid fiber are present transverse to the yarns comprising crystallized meta-aramid fiber.
14. The fabric of claim 13 wherein the yarns comprising crystallized meta-aramid fiber are pigmented, dyed, or colored.
15. The fabric of claim 13 wherein the yarns comprising amorphous meta-aramid fiber are dyed.
16. A protective article comprising the fabric of claim 13 .
17. The fiber of claim 8 wherein the meta-aramid fiber is present in a range from 60 to 75 weight percent.