Method of producing metal article having internal passage coated with a ceramic coating
View Patent ↗The present application relates to a method of producing a metal article having an internal passage coated with a ceramic coating. The method comprises: preparing a core for defining the internal passage; applying the ceramic coating on the core; assembling the core with the ceramic coating applied thereon into a mold; casting metal into the mold at a pour temperature lower than the melting temperature of the ceramic coating; and removing the core. The ceramic coating may be applied by plasma spraying or slurry deposition.
1. A method of producing a metal article having an internal passage coated with a ceramic layer acting as a thermal barrier, said method comprising the following steps:
preparing a core for defining the internal passage;
applying the ceramic coating on the core;
assembling the core with the ceramic coating applied thereon into a mold;
casting metal into the mold at a pour temperature lower than the melting temperature of the ceramic coating;
removing the core; and
strengthening the ceramic coating after the removal step by infiltrating the coating with colloidal or sol gel zirconia, alumina, or silica.
2. A method according to claim 1 , wherein the step of applying the ceramic coating is performed by a thermal spray process.
3. A method according to claim 1 , wherein the step of applying the ceramic coating is performed by a slurry deposition process.
4. A method according to claim 1 , wherein the ceramic coating comprises stabilized zirconia, stabilized hafnia, alumina, or zircon.
5. A method according to claim 1 , further comprising a step of applying a metallic or intermetallic coating on the ceramic coating prior to casting.
6. A method according to claim 5 , wherein the metallic or intermetallic coating contains one or more of Al, Cr, Y, Si, Hf, Co, and Fe.
7. A method according to claim 1 , wherein the core is a resin-bonded sand core or a graphite core which is removed by oxidation.
8. A method according to claim 1 or 7 , wherein a temporary coating is applied on the core before applying the ceramic coating, and wherein the removal step includes removing both the core and the temporary coating.
9. A method of producing a metal article having an internal passage coated with a ceramic layer acting as a thermal barrier, said method comprising the following steps:
preparing a core for defining the internal passage:
applying a temporary coating of Mo or MoC onto the core;
applying the ceramic coating onto the temporary coating on the core;
assembling the core with the temporary and ceramic coatings applied thereon into a mold;
casting metal into the mold at a pour temperature lower than the melting temperature of the ceramic coating; and
removing the core and the temporary coating.
10. A method according to claim 1 , wherein the cast metal comprises stainless steel, or a nickel, cobalt or iron based superalloy, or an aluminum alloy.
11. A method according to claim 1 , wherein the metal article is a turbine housing unit for a turbocharger of an internal combustion engine, a combustion chamber, a duct for hot gases, or a rocket nozzle or thruster.