Calcium phosphate cements and methods for using the same
View Patent ↗Methods and compositions for producing flowable compositions, e.g. pastes, that set into calcium phosphate products are provided. In the subject methods, dry reactants that include a calcium source and a phosphate source are combined with setting fluid to produce the flowable composition. A feature of the subject methods is that the dry reactants include a particulate calcium and/or phosphate reactant having a mean particle size of less than about 8 μm and narrow size distribution. Also provided are the compositions themselves as well as kits for use in practicing the subject methods. The subject methods and compositions produced thereby find use in a variety of applications, including the repair of hard tissue defects, e.g., bone defects.
1. A method of producing a flowable composition that sets into a solid calcium phosphate containing product, said method comprising:
combining:
(a) a setting fluid, wherein said setting fluid is a solution of a water soluble silicate; and
(b) a dry reactant component comprising an air pulverized first particulate calcium and/or phosphate reactant having a mean particle size of about 8 μm or less and narrow particle size distribution;
in a ratio of said (a) to (b) sufficient to produce said flowable composition that has a setting value of at least about 200 Newtons in 3 minutes.
2. The method according to claim 1 , wherein said dry reactant component consists of said first particulate calcium and/or phosphate reactant.
3. The method according to claim 1 , wherein said dry reactant component comprises a second calcium and/or phosphate reactant having a mean particle size that is about 10 μm or greater.
4. The method according to claim 3 , wherein the ratio of said first to second calcium and/or phosphate reactants in said dry reactant component ranges from about 1 to about 10.
5. The method according to claim 1 , wherein said first particulate calcium and/or phosphate reactant is a calcium phosphate compound.
6. The method according to claim 5 , wherein the ratio of calcium to phosphate of said calcium phosphate compound ranges from about 1 to about 2.
7. The method according to claim 6 , wherein said calcium phosphate compound is a tricalcium phosphate.
8. The method according to claim 1 , wherein said first particulate calcium and/or phosphate reactant has a mean particle size of about 4 μm.
9. The method according to claim 8 , wherein said flowable composition is a paste.
10. The method according to claim 8 , wherein said flowable composition is a clay.
11. A flowable composition that sets into a solid calcium phosphate containing product, wherein said composition is produced by a method comprising:
Combining:
(a) a setting fluid, wherein said setting fluid is a solution of a water soluble silicate; and
(b) a dry reactant component comprising an air pulverized first particulate calcium and/or phosphate reactant having a mean particle size of about 8 μm or less and narrow particle size distribution;
in a ratio of said (a) to (b) sufficient to produce said flowable composition that has a setting value of at least about 200 Newtons in 3 minutes.
12. The composition according to claim 11 , wherein said composition is a paste.
13. The composition according to claim 11 , wherein said composition is a clay.
14. A method of repairing a hard tissue defect, said method comprising:
applying to the site of said defect a flowable composition that sets into a solid calcium phosphate containing product, wherein said composition is produced by a method comprising:
Combining:
(a) a setting fluid, wherein said setting fluid is a solution of a water soluble silicate; and
(b) a dry reactant component comprising an air pulverized first particulate calcium and/or phosphate reactant having a mean particle size of about 8 μm or less and narrow particle size distribution;
in a ratio of said (a) to (b) sufficient to produce said flowable composition that has a setting value of at least about 200 Newtons in 3 minutes.
15. The method according to claim 1 , wherein said mean particle size ranges from about 1.0 μm to about 7.0 μm.
16. The method according to claim 1 , wherein said mean particle size ranges from about 1.0 μm to about 6.0 μm.
17. The method according to claim 1 , wherein said mean particle size ranges from about 1.0 μm to about 5.0 μm.
18. The method according to claim 1 , wherein said narrow particle size distribution comprises a standard deviation of about 2.0 μm to about 4.0 μm.