Railroad tie and method for making same
View Patent ↗Thermoplastic polymers, rubbery polymeric components and reinforcing fillers are mixed and heated to a range of 380° F. to 440° F. The resulting mixture is then fed into a Banbury mixer, with the resulting mixture fed into a diverter feeding two molds. The velocity of the piston of each mold being filled is controlled to thereby control the density of the molded product along its length. As each mold is filled, it is deposited in a cool water bath (50° F.-60° F.) while the next mold is being filled. The molds are sequentially transferred to an air cooling rack to complete the process. A texture, generally comprising indentations perpendicular to the longitudinal axis on the molded object, provides a frictional surface between the railway crosstie and the ballast beneath the crosstie.
1. A process for forming a molded member for use as a railroad tie, lumber or other structural member having a varied or constant density, comprising the steps of:
mixing a thermoplastic polymer component until it forms a flowable mixture;
using a closed chamber mixer to mix said mixture;
feeding said mixture into a mold, said mixture at least partially filling said mold;
using an extruder between said closed chamber mixer and said mold to transport said mixture to said mold;
controlling the density of said extrudable material during the filling of said mold; and
wherein a piston is included in said mold, and the pressure associated with the movement of the piston is used to control said density.
2. The process of claim 1 , further comprising the step of mixing a filler component with said thermoplastic polymer component until said components form a flowable mixture.
3. The process of claim 1 , further comprising the step of mixing a rubbery polymeric component with said thermoplastic polymer component until said components form a flowable mixture.
4. The process of claim 1 , further comprising the steps of:
removing said member from said mold;
cooling said member by air cooling; and
rotating said member during air cooling at least once, whereby said rotation prevents warpage.
5. A process for forming a molded member for use as a railroad tie, lumber or other structural member having a varied or constant density, comprising the steps of:
using a closed chamber mixer to mix a rubbery polymeric component until it forms a flowable mixture;
feeding said mixture into a mold, said mixture at least partially filling said mold;
using an extruder between said mixer and said mold to transport said mixture to said mold;
controlling the density of said extrudable material; and
wherein a piston is included in said mold, and the pressure associated with the movement of the piston is used to control said density.
6. The process of claim 5 , further comprising the step of mixing a filler component with said rubbery polymeric component until said components form a flowable mixture.
7. The process of claim 5 , further comprising the step of mixing a thermoplastic polymer component with said filler and said rubbery polymeric component until said components form a flowable mixture.
8. The process of claim 5 , further comprising the steps of:
removing said member from said mold;
cooling said member by air cooling; and
rotating said member during air cooling, whereby said rotation prevents warpage.