Method for pretreating a piezoelectric ceramic and method for adjusting an injection valve
View Patent ↗In a method for pretreating a piezoelectric ceramic ( 1 ) and a method for adjusting an injection valve ( 7 ), the piezoelectric ceramic ( 1 ) is exposed to environmental conditions, leading to a reduction of polarization and also a reduction of the length of the ceramic ( 1 ). The obtained length exhibits a greater long-term stability due to said adjusting phase. Consequently, the injection valve ( 7 ) can be re-adjusted before use. As a result, renewed adjustment thereof is required only after a long period in service.
1. A method for pretreating a piezoelectric ceramic which can be used for installing in an injection valve, comprising the steps of:
providing a piezoelectric ceramic stack;
subjecting the piezoelectric ceramic stack to a temperature treatment, wherein the temperature is set from 60° C. to 200° C. for a first predeterminable period of time; and
during the temperature treatment subjecting the piezoelectric ceramic stack to a polarization process during which with increasing time a polarization voltage applied to the piezoelectric ceramic stack is increased from an initial value to a maximum value.
2. The method according to claim 1 , wherein the first period of time amounts to between 0.5 and 2.5 hours.
3. The method according to claim 1 , wherein the temperature lies in the range from 60° C. to 180° C.
4. The method according to claim 1 , wherein the piezoelectric ceramic stack is mechanically prestressed during the temperature treatment.
5. The method according to claim 1 , wherein the polarization is conducted with a voltage of from 50 to 170 volts.
6. The method according to claim 5 , wherein the polarization is conducted with a pulsed direct-current voltage.
7. The method according to claim 6 , wherein the polarization is conducted with a frequency of from 20 to 120 Hz.
8. The method according to claim 5 , wherein the polarization is conducted over a period of from 50 to 150 seconds.
9. The method according to claim 5 , wherein the maximum voltage is held constant for a second predetermined period of time.
10. The method according to claim 1 , wherein the injection valve has a piezoelectric actuator comprising the piezoelectric ceramic stack, the actuator having a defined position or prestress in relation to a control element of the injection valve, further comprising the steps of:
operating the injection valve in an adjustment phase at least with one parameter which occurs when an internal combustion engine is running; and
setting the actuator after the adjustment phase to a defined position or prestress.
11. The method according to claim 10 , wherein the injection valve is installed in an internal combustion engine, and the injection valve is used in the adjustment phase for injecting fuel.
12. The method according to claim 10 , wherein the injection valve is connected to a fuel reservoir, the fuel reservoir holds fuel ready at a predeterminable pressure for injecting and the pressure lies preferably in a range which corresponds to a maximum range when the internal combustion engine is running.
13. The method according to claim 10 , wherein the actuator for injecting fuel is driven with a high frequency which corresponds to a high engine speed of the internal combustion engine.
14. The method according to claim 10 , wherein the internal combustion engine is run at a temperature, in particular in the region of the piezoelectric ceramic stack, which lies in the mean to upper temperature range of the temperatures occurring when the internal combustion engine is running.
15. A method for pretreating a piezoelectric ceramic which can be used for installing in an injection valve, comprising the steps of:
providing a piezoelectric ceramic stack;
subjecting the piezoelectric ceramic stack to a temperature treatment, wherein the temperature is set from 60° C. to 200° C. for a first predeterminable period of time; and
subsequently subjecting the piezoelectric ceramic stack to a polarization process during which with increasing time a polarization voltage applied to the piezoelectric ceramic stack is increased from an initial value to a maximum value.
16. The method according to claim 15 , wherein the first period of time amounts to between 0.5 and 2.5 hours and the temperature lies in the range from 60° C. to 180° C.
17. The method according to claim 15 , wherein the piezoelectric ceramic stack is mechanically prestressed during the temperature treatment.
18. The method according to claim 15 , wherein the polarization is conducted with a voltage of from 50 to 170 volts.
19. The method according to claim 15 , wherein the polarization is conducted with a pulsed direct-current voltage having a frequency of from 20 to 120 Hz.
20. The method according to claim 15 , wherein the polarization is conducted over a period of from 50 to 150 seconds.
21. The method according to claim 15 , wherein the maximum voltage is held constant for a second predetermined period of time.
22. The method according to claim 15 , wherein the injection valve has a piezoelectric actuator comprising the piezoelectric ceramic stack, the actuator having a defined position or prestress in relation to a control element of the injection valve, further comprising the steps of:
operating the injection valve in an adjustment phase at least with one parameter which occurs when an internal combustion engine is running; and
setting the actuator after the adjustment phase to a defined position or prestress.