Method of removing impurities from a SrB
View Patent ↗An acidic solution can be used to dissolve undesirable impurity phases in UV-emitting SrB 4 O 7 :Eu phosphors that reduce the UV emission intensity of said phosphor. In particular, the impurity phase, SrB 6 O 10 :Eu, is no longer detected after treating the phosphor with an acid washing process. The phosphors after acid washing are shown to have improved UV emission intensity without greatly increasing the mean particle size.
1. A method of removing impurities from a SrB 4 O 7 :Eu phosphor, the method comprising:
(a) adding a SrB 4 O 7 :Eu phosphor containing a SrB 6 O 10 :Eu impurity phase to an acidic solution;
(b) dissolving the SrB 6 O 10 :Eu impurity phase; and
(c) separating the phosphor from the dissolved impurity.
2. The method of claim 1 wherein the acidic solution has a pH of from about 0.8 to about 1.5.
3. The method of claim 1 wherein the acidic solution contains nitric acid.
4. The method of claim 1 wherein the pH of the acidic solution is greater than about 4 after the impurity phase is dissolved.
5. The method of claim 2 wherein the solution is heated to a temperature from about 65° C. to about 70° C. to dissolve the impurity phase.
6. A method of removing an SrB 6 O 10 :Eu impurity phase from a SrB 4 O 7 :Eu phosphor, the method comprising:
(a) forming a slurry of a nitric acid solution and the SrB 4 O 7 :Eu phosphor containing the SrB 6 O 10 :Eu impurity phase;
(b) dissolving the SrB 6 O 10 :Eu impurity phase; and
(c) separating the phosphor from the dissolved impurity.
7. The method of claim 6 wherein the nitric acid solution has a pH of from about 0.8 to about 1.5 prior to forming the slurry.
8. The method of claim 6 wherein the pH of the solution is greater than about 4 after the impurity phase is dissolved.