Method for processing elemental sulfur-bearing materials using high temperature pressure leaching
View Patent ↗The present invention relates generally to a process for the production of sulfuric acid and liberation of precious metal values from materials containing sulfur through pressure leaching operations. In accordance with various aspects of the present invention, the sulfur-bearing materials may comprise residues from pressure leaching operations, such as those carried out at medium temperatures. The process of the present invention can be advantageously used to convert such sulfur-bearing materials to sulfuric acid by means of pressure leaching. The sulfuric acid so produced can be used beneficially in other mineral processing operations, for example those at the site where it is produced. Metals, such as precious metals, that are contained within the sulfur-bearing materials advantageously may be recovered from processing products by established precious metals recovery technology.
1. A treatment process comprising the steps of:
a) providing a feed stream comprising an elemental sulfur-bearing material and a dispersant wherein said dispersant comprises at least one of a surfactant, ground sand, mineral processing tailings, or combination thereof, and wherein said elemental sulfur-bearing material comprises an elemental sulfur-containing residue from a pressure leaching operation carried out at a temperature in the range of about 140° C. to about 180° C.;
b) pressure leaching at least a portion of said feed stream at a temperature in the range of about 220° C. to about 275° C. in an oxygen-containing atmosphere in an agitated multiple-compartment pressure leaching vessel to form a product slurry comprising a sulfuric acid solution;
c) separating at least a portion of said sulfuric acid solution from said product slurry to yield a residue;
d) recovering at least one metal value from said residue.
2. The process of claim 1 wherein said step of recovering at least one metal value from said residue comprises recovering at least one precious metal from said residue.
3. The process of claim 1 wherein said step of pressure leaching at least a portion of said feed stream comprises pressure leaching at temperatures above about 235° C.
4. A treatment process comprising the steps of:
a) providing a feed stream comprising an elemental sulfur-bearing material-wherein said elemental sulfur-bearing material comprises an elemental sulfur-containing residue from a pressure leaching operation carried out at a temperature in the range of about 140° C. to about 180° C.;
b) pressure leaching at least a portion of said feed stream in the presence of a dispersant wherein said dispersant comprises at least one of a surfactant, ground sand, mineral processing tailings, or combination thereof, at a temperature in the range of about 220° C. to about 275° C. in an oxygen-containing atmosphere in an agitated multiple-compartment pressure leaching vessel to form a product slurry comprising a sulfuric acid solution;
c) separating at least a portion of said sulfuric acid solution from said product slurry to yield a residue;
d) recovering at least one metal value from said residue.
5. The process of claim 4 wherein said step of recovering at least one metal value from said residue comprises recovering at least one precious metal from said residue.
6. A process for recovering metal values from an elemental sulfur-bearing solid residue of a pressure leaching process carried out at a temperature in the range of about 140° C. to about 180° C. the process comprising the steps of:
a) comminuting the elemental sulfur-bearing solid residue from the pressure leaching process carried out at a temperature in the range of about 140° C. to about 180° C. to produce a feed material;
b) forming a feed slurry by combining said feed material with a dispersant wherein said dispersant comprises at least one of a surfactant, ground sand, mineral processing tailings, or combination thereof, and a sufficient amount of fluid medium;
c) pressure leaching at least a portion of said feed slurry at a temperature in the range of about 220° C. to about 275° C. in an oxygen-containing atmosphere to yield a pressure leach product slurry comprising a sulfuric acid solution;
d) reducing the temperature and pressure of said product slurry;
e) separating at least a portion of said sulfuric acid solution from said product slurry to yield a solid residue;
f) recovering at least one metal value from said solid residue.
7. The process of claim 6 wherein said step of recovering at least one metal value from said solid residue comprises recovering one or more precious metals contained in said residue.
8. The process of claim 6 wherein said step of reducing the temperature and pressure of said product slurry comprises flashing said product slurry.
9. The process of claim 6 , said process further comprising the step of utilizing at least a portion of said sulfuric acid solution in connection with other processing operations.
10. The process of claim 6 wherein said step of pressure leaching at least a portion of said feed slurry is conducted at a temperature in the range in excess of about 235° C.
11. A process for the production of sulfuric acid and recovery of precious metals from an elemental sulfur-bearing material comprising the steps of:
a) providing an elemental sulfur-bearing material wherein said elemental sulfur-bearing material comprises an elemental sulfur-containing residue from a pressure leaching operation;
b) pressure leaching said elemental sulfur-bearing material at a temperature in the range of about 220° C. to about 275° C. in an oxygen-containing atmosphere in an agitated multiple-compartment pressure leaching vessel to form a product slurry comprising a sulfuric acid solution;
c) adding a dispersant during said pressure leaching step wherein said dispersant comprises at least one of a surfactant, ground sand, mineral processing tailings, or combination thereof;
d) separating at least a portion of said sulfuric acid solution from said product slurry to yield a solid residue;
e) recovering at least one precious metal value from said solid residue.
12. The process of claim 11 wherein said step of providing an elemental sulfur-bearing material comprises providing an elemental sulfur-containing residue from a pressure leaching operation carried out at a temperature in the range of about 140° C. to about 180° C.
13. The process of claim 11 wherein said step of pressure leaching comprises pressure leaching at a temperature of about 235° C.