Use of organomodified siloxanes for surface modification of polyolefins
View Patent ↗The invention provides for the use of organomodified polysiloxanes of the general formula (I) in which R 1 independently at each occurrence is an aliphatic or aromatic C 1-20 hydrocarbon radical, R 2 , R 2* independently of one another are R 1 or are aliphatic, saturated or unsaturated C 1-60 hydrocarbon radicals, optionally containing functional groups, a=1 to 500, preferably <100, in particular 5 to 50, b=0 to 50, preferably <20, in particular <10, c=0 to 50, preferably 0 to 10, in particular 0 as additives for surface enhancement in polyolefins.
1. A method for improving surface properties of filled or unfilled polyolefin films which comprises adding about 0.001 to about 5% by weight, based upon polyolefin polymer, organomodified polysiloxanes of the formula
in which
R 1 independently at each occurrence is an aliphatic or aromatic C 1-20 hydrocarbon radical,
R 2 , R 2* independently of one another are R 1 or are aliphatic, saturated or unsaturated C 1-60 hydrocarbon radicals, optionally containing functional groups,
a=1 to 500,
b=0 to 50,
c=0 to 50
to the polyolefin polymer and extruding the polymer,
wherein the organomodified siloxanes are prepared by dehydrogenerative coupling.
2. The method according to claim 1 , wherein the surface properties are friction coefficient, scratch resistance, roughness, water repellency, weathering stability, slip properties, release effect, and/or abrasion resistance.
3. The method according to claim 1 , wherein at least 90% of the radicals R 1 in the organomodified polysiloxanes are methyl radicals.
4. The method according to claim 1 , wherein a in the organomodifled polysiloxanes is 5 to 100 and b and c=0.
5. The method according to claim 1 , wherein a in the organomodified polysiloxanes is 10 to 50 and b and c=0.
6. The method according to claim 1 , the amount of organomodified polysiloxanes is between about 0.01% to about 5% by weight, based on the polymer.
7. The method according to claim 1 , wherein the polymer film is polyethylene, polypropylene, or polyamide film.
8. The method according to claim 1 , wherein the amount of organomodified polysiloxanes is between about 0.1% to about 5% by weight, based on the polymer.